PVDF Membrane has been used as material for the UF membrane through in-situ interfacial polymerization (IP) because of it’s outstanding properties such as high chemical resistance, thermal stability, and mechanical strength. In this study, surface morphology change of PVDF membrane was researched depending on evaporation time. 13% PVDF 6020 was used for casting and the evaporation time period was from 5s to 600s. The surface morphology of the membrane was investigated by scanning electron microscopy (SEM) and filtration was conducted in the cross flow method to evaluate the a performance of UF membrane. As a result, average pore size was increased with longer evaporation times which caused the decrease of rejection.

뛰어난 물성을 가진 poly (vinylidene fluoride) (PVDF)는 정밀여과 (MF)와 한 외여과 (UF) 분리막의 소재로써 많이 연구되고 있다. 기공의 크기를 조절하는 것은 분리막을 제조하는데 있어 중요한 요소이다. 본 연구에서는 매우 간단한 방법으로 분리막의 기공 크기를 조절하는 새로운 방법을 제시하고자 한다. PVDF 한외여과 분리막의 기공 크기는 유리판 위에 150 ㎛의 두께로 주조된 PVDF 도프 용액이 응고조 (증류수)속으로 들어가는 속도를 통해 조절되었다. 이 때 PVDF 한외여과 분리막의 기공 크기는 응고조에 들어가는 PVDF 도프 용액의 속도가 감소될수록 증가하는 경향을 보였다.