Tensile strength was investigated for hybrid bar (HYB), in this study. HYB is made of both steel reinforcement and glass fiber. Cross section of HYB has a shape in which steel reinforcement wrapped with glass fiber. For the production of HYB, rebar of SD400 class and glass fiber of E class are used as main materials. Vinyl ester resin is used to harden a glass fiber. In order to evaluate for tensile strength of HYB, the direct tensile test was performed about total ten specimens. The length of total specimens is 2,200 mm including the grip. Diameter of HYB according to core diameter was considered as a test variable. Direct tensile test for HYB was performed using a UTM with a capacity of maximum 1,000 kN. Tensile strength and strain were measured for each specimen during the test. From the test results, tensile strength and elastic modulus were 317 ~ 341 MPa, 103 ~ 107 GPa, respectively. Especially, elastic modulus of HYB was improved in comparison with usual GFRP bars such as the Aslan 100 or the V-rod.

최근 철근 콘크리트 구조물에 다양한 철근 이음이 사용되고 있다. 이에 따라 커플러 이음 철근의 인장 특성에 대한 파악이 중요해졌 다. 본 연구에서는 커플러 이음 철근의 연성도에 대한 평가를 위하여 ASTM A615 기준에 따라 생산된 Grade 60 D22(#7), D29(#9), 그리고 두 종류의 커플러를 상대로 1축 인장시험을 수행하였다. 보다 정확하고 다양한 지점에서 자유로운 계측이 가능한 이미지 프로세싱 방법을 사용하 여 변형률을 계측하였다. 1축 인장시험 결과, 응력-변형률 관계와 응력 단계별 종방향 변형률 분포를 산출할 수 있었고, 이를 통하여 동일한 표 점거리 내에서 커플러 이음 부분이 많이 차지할수록 평균변형률이 낮아지는 것을 알 수 있었다. 또한 커플러 이음철근의 극한거동 및 파단 시 변형률에 대한 평가를 통해 커플러의 길이에 대한 한계상태변형률과 파단변형률과의 상관관계를 정식화하였다.