The composites fabricated by powder in sheath rolling method were cold-rolled by 50% reduction and annealed for 1.8 ks at various temperatures ranging from 200 to 50, for improvement of the mechanical properties. The mechanical properties and texture of the composites after rolling and annealing were investigated. The tensile strength of the composites increased significantly due to work hardening after cold rolling, however it decreased due to restoration after annealing. The strength of the composites was improved by thermo mechanical treatment. On the other hand, the texture evolution with annealing temperatures wa,i different between the unreinforced material and the composites. The unreinforced material showed a deformation (rolling) texture of which main component is ｛112｝<111> at annealing temperatures up to 30. However, the composites have already exhibited a recrystallization texture of which main component is ｛001｝<100> after annealing at 20. This proves that the critical temperature for recrystailization is lower in the composites than in the unreinforced ones.

가공열처리에 의한 결정립계조절 개념을 이용하여 Alloy 600 재료의 결정립계특성과 부식특성을 조사하였다. 가공열 처리에 따른 결정립계특성 변화를 EBSP로 분석하였으며, 결정립계특성 변화가 입계부식 및 응력부식균열 거동에 미치는 영향을 평가하였다. 가공열처리 반복에 따른 각 단계에서의 CSL 입계의 분율 변화가 두드러지지는 않았으나, 상용재료에 비하여 CSL 분율이 약 10% 이상 향상된 결과를 얻었다. 결정립계특성 변화에 따라 입계부식 저항성이 현저하게 증가하였으나, 1차측 응력부식균열 특성에 있어서는 가공열처리를 반복할수록 파단시간과 최대하중이 감소하고 평균 균열성장속도가 증가하였으며 2차 균열이 억제되는 결과를 얻었다. 결정립계의 'fine tuning' 기구가 이러한 부식거동변화에 작용한 것으로 해석할 수 있었다.