Flexible dye-sensitized solar cells using binder free TiO2 paste for low temperature sintering are developed. In this paste a small amount of titanium gel is added to a paste of TiO2 nanoparticle. Analysis of titanium gel paste prepared at 150 ℃ shows that it has a pure anatase phase in XRD and mesoporous structure in SEM. The formation of the titanium gel 1- 2 nm coated layer is confirmed by comparing the TEM image analysis of the titanium gel paste and the pristine paste. This coating layer improves the excited electron transfer and electrical contact between particles. The J-V curves of the organic binder DSSCs fabricated at 150℃ shows a current density of 0.12 mA/cm2 and an open-circuit voltage of 0.47 V, while the titanium gel DSSCs improves electrical characteristics to 5.04 mA/cm2 and 0.74 V. As a result, the photoelectric conversion efficiency of the organic binder DSSC prepared at low temperature is as low as 0.02 %, but the titanium gel paste DSSCs has a measured effciency of 2.76%.

본 연구에서는 0.5, 1.0, 1.5 wt%의 TiO2를 함유하는 인듐-티타늄 수산화물을 졸 및 염기 첨가에 의해 얻었고, 200oC와 500oC에서 겔화 과정을 통해 ITiO(Indium Titanate Oxide)를 얻었다. 200oC에서 겔화 과정 후 얻어지는 ITiO 입자가 작아서 조밀성이 있는 ITiO 타겟을 제조하였다. 0.5, 1.0, 1.5 wt%의 TiO2를 함유하는 ITiO 타겟을 스퍼터링하여 ITiO 박막을 유리판위에 제작하여 비저항, 전하 이동도, 캐리어 농도를 조사하였다. 이들 박막 중에서 산소 조성이 0.4 %인 조건에서 0.5 wt% 중량% TiO2를 함유하는 ITiO 타겟으로부터 제작된 ITiO 박막이 가장 낮은 비저항, 가장 큰 전하이동도 및 가장 낮은 캐리어 농도를 보임을 알 수 있었고, 얻어진 ITiO 박막의 광투과율을 측정하여 적외선 영역에서 광투과율이 ITO(Indium Tin Oxide) 박막에 비해 현저히 증가함을 발견하였다.