Many researchers have defined critical chloride content as a specific value. The studies reporting critical threshold chloride content have involved the experimental measurement of the average amount of the total chloride content. The studies have tried to define the critical chloride content within the scope of their experimental concrete mix proportion at arbitrary time. However, there is no agreement on its value. The purpose of this study is to explore the combined effect of oxygen and chloride on reinforcement corrosion. In the experimental recipe, water soluble oxygen is taken into account to define the critical chloride content. Corrosion current density of reinforcement was measured by linear polarization resistance method.

The concrete frames are deteriorated by the corrosion of reinforcement bars. To consider the corrosion effect on the seismic performance of concrete frames, the probabilistic approach method such as the Monte Carlo simulation (MCS) is utilized. However, MCS has a weakness that a lot of computation time is required. In this study, the evaluation method for the seismic performance of chloride-corroded reinforced concrete moment frames using multi-cores is presented to reduce the computation time.

The volume expansion of corroded steel reinforcement produces tensile stress on the surrounding concrete, which causes splitting cracking of concrete cover, and deteriorates the service ability and durability of reinforced concrete(RC) members. In addition, since the steel corrosion induces bond strength degradation between steel bar and concrete, the structural performance of RC members can be deteriorated significantly. In this study, the theoretical study was performed to probe the mechanism of the bond strength reduction due to steel corrosion. The bond strength between corroded steel bar and concrete was calculated by mathematically formulating the expansion pressure of corroded steel reinforcement. The proposed model was verified by comparing with the existing test results, and it showed that the proposed model estimate the bond strength reduction of corroded RC elements very closely.

Existing nondestructive test methods used to measure reinforcement corrosion is based on qualitative measurement of corrosion, and it has many difficulties of use because many equipment and measurement stages are required for application at actual sites. Accordingly, this study was conducted to estimate reinforcement corrosion of concrete structures using infrared thermography method as a method of measuring reinforcement corrosion in concrete. As for the specimen was to measure reinforcement corrosion, D13 reinforcement with size of 200×150×180mm was buried at length of 250mm for covering depth of 20mm and 40mm. Accelerated reinforcement corrosion test was carried out after placement of concrete. As a result of measuring reinforcement corrosion using infrared thermography method, temperature difference of 1~3°C was shown depending on the corrosion stage. There was a correlation in which temperature decreased according to chloride content. Infrared thermography method was confirmed as a useful method for measurement of reinforcement corrosion inside concrete.

In this study, the inhibitive effect of electrochemical treatment subjected to fresh and hardened concrete and literature reviews in terms of the treatment were performed. In hardened concrete, chloride ions are mixed during casting to destroy the passivity of steel, and then the current was provided for 2 weeks with 250, 500 and 750 mA/m2. After completion of electrochemical treatment, the extraction of chloride ions was quantified and repassivation of steel was observed. Simultaneously, the equated levels of current density for 2 weeks were applied to fresh concrete. Steel-concrete interface in concrete was observed by BSE image analysis and the concrete properties in terms of the diffusivity of chloride ions and the resistance of steel corrosion was measured. As the result, electrochemical treatment is very effectiveness to rehabilitate the passive film on the steel surface and 63-73% of chloride ions in concrete were extracted by the treatment. As the treatment was applied to fresh concrete, the resistance of steel corrosion was improved due to the densification of Ca(OH)2 layers in the vicinity of steel. However, an increase in the current density resulted in an increase in surface chloride content of concrete.

To assess the steel corrosion resistance for Calcium aluminate cement and Ordinary portland cement against internal chloride ions, mortar specimens were cast, assuming aggregates are inert. Linear polarisation, half-cell potential and mass loss were chosen to measure the rate of steel corrosion.

The durability of structures that has been built along the coastline based on the national geographic characteristics became a very important standard in economic and societal aspects. The environment that the steel corrosion would most likely happen is called tidal zone. It is a well-known zone and lots of researches have been done. We decided to implement steel corrosion monitoring on artificial seawater to find what kind of environment accelerates the steel corrosion. We compared and analyzed the experiment through galvanic potential measurement and half cell potential measurement

To evaluate the decline of the strength and energy dissipation capacity of RC moment frame, which proceeded with corrosion of the reinforced-bar of the element, simulation test is conducted with simulation model which adopted monte-carlo simulation method. For the design of damper, the strength, stiffness degradation and energy dissipation capacity are evaluated by using test results.

The main factor which makes RC structures weakening is corrosion of reinforced-bar that inserted in elements of the structure, and there are many researches that trying to figure out how to prevent degradation of strength of the re-bar. Because of that various factors effect on the deterioration of RC structures complexly, this paper suggest the indicator which can assess the failure probability of the structures.

콘크리트내의 철근의 부식은 열화와 콘크리트 구조물의 조기파괴의 주된 원인이 된다. 본 연구에서는 비파괴 기법 중 전자기적 열유도방법과 적외선 열화상기법을 이용한 철근부식평가가 시도되었는데, 부식 또는 비부식된 철근의 열특성 차이를 이용한 것이다. 본 논문은 이러한 개념을 배경으로 수행한 실험적 연구이며, 유도전류를 통해 콘크리트 표면으로부터 내부 철근을 가열하고 외부의 적외선 카메라를 이용하여 표면의 온도변화를 관측한다. 피복두께가 다른 콘크리트 시편은 앞면과 배면의 피복두께를 동일하게 제조하여 앞면에서 가열과 배면에서의 온도측정을 동시에 할 수 있도록 고안되었다. IC (Impressed Current) 방법을 통하여, 철근 부식을 촉진하였으며, 적외선 화상을 통하여 온도가열과 냉각을 전 시험과정에 걸쳐 측정하였다. 본 실험을 통하여 부식/비부식 철근의 뚜렷한 온도변화를 확인하였으며, 부식된 시편에서 빠른 온도증가속도 및 냉각속도를 평가하였다. 본 연구는 콘크리트 매립철근의 비파괴적인 부식탐지의 가능성을 보여주고 있다.

콘크리트 내부에 매설된 철근의 부식은 철근콘크리트구조물의 조기 성능저하와 붕괴의 주요원인이 되고 있다. 철근콘크리트 구조물에 발생하는 열화현상 중에서 철근부식에 의해 발생되는 염해는 그 피해가 다른 열화 현상보다 심하고 구조물의 보수 및 시공 측면에서도 막대한 경비가 요구되고 보수시기 또한 정하기 힘들다. 따라서 철근의 부식상태에 대한 조기발견은 관리자의 효율적인 보수 및 보강계획 수립을 위해 매우 중요하다. 한편 철근 부식을 평가하는 방법 중 비파괴측정이 많이 사용되고 있다. 특히 CM-Ⅱ(corrosion meter) 측정기는 자연전위와 분극저항 및 콘크리트 비저항을 측정할 수 있어서 많이 사용되지만 몇 가지 단점을 가지고 있다. 이러한 단점을 극복하기 위해 매립형 미니센서가 개발되어져 왔다. 이 미니센서를 이용하여 철근 부식을 측정한 후 CM-Ⅱ(corrosion meter)의 측정결과와 비교분석하여 개발된 미니센서의 타당성을 검증하였다.

철근부식에 의해 발생된 녹은 철근 주위의 콘크리트에 팽창압력을 발생시켜 콘크리트의 균열유발, 피복콘크리트의 박리나 탈락, 철근의 단면적 감소들을 야기 시킨다. 또한 철근콘크리트 구조물 내에 매입된 철근의 부식은 철근과 콘크리트의 일체 거동을 저하시킴으로써 구조물이 외력에 견딜 수 있는 구조성능의 감소를 초래한다. 본 논문에서는 3차원 스캐너를 이용하여 철근이 부식됨에 따른 철근의 표면적을 측정하여 부식률과 표면 거칠기와의 관계를 파악하였다. 철근부식률 1~2%의 경우에서는 철근 표면적이 증가하는 것으로 나타났다. 이는 동일 범위내에서 철근의 부착강도가 증가한 기존의 실험결과와 매우 유사한 결과를 나타낸다. 철근부식률 2% 이상에서는 오히려 표면적이 감소하였으며, 이는 단면적 손실로 인한 기존 부착강도 실험과 부합되는 결과를 나타냈다

시멘트 대체 재료로서 플라이애쉬의 사용은 시멘트 생산비용을 절감시키는 효과를 창출하였다. 반면에 플라이애쉬 혼입콘크리트는 OPC에 비해 상대적으로 긴 양생시간과 초기강도의 발현 저하를 들 수 있어 이의 해결을 위해 물리적 방법, 온도 및 화학적 방법 등과 같은 다양한 활성화 기술의 적용을 통하여 플라이애쉬 혼입 콘크리트의 수화를 가속시킬 수 있고, 콘크리트의 부식 저항성을 향상시킬 수가 있다. 본 연구에서는 10～40%의 치환률을 가진 활성화된 플라이애쉬 시편을 통해 개방 회로형 전위측정(Open circuit potential measurement)을 수행하였고, 투수시험, 급속염화물침투시험 및 SEM(Scanning electron microscopy)촬영을 통해 OPC 콘크리트와 비교․분석 하였다. 또한, 치환률의 임계범위 20～30%의 경우에 있어서 활성화된 플라이애쉬를 사용한 콘크리트가 열화저항성에 있어서 개선효과가 나타나고 있음을 확인하였다. 또한 플라이애쉬를 화학적으로 활성화시킨 경우가 본 연구에서 수행된 다른 활성화 방법들에 비해 더욱 좋은 결과를 나타나고 있음도 확인하였다.

피복 콘크리트의 균열 발생에 기인한 매크로셀 부식 환경하에서의 Cr강방식철근의 방식성을 평가하기 위하여 10종류의 Cr강방식철근을 콘크리트에 매입 후 피복 콘크리트에 모사 균열을 발생시킨 공시체를 제작하였다. 그 후 염수 분무 촉진 양생 105사이클까지의 매크로셀 부식전류밀도의 경시변화와 아노드ㆍ캐소드 철근의 자연전위, 부식면적률, 부식감량률을 측정함으로써 Cr강방식철근의 방식성에 대하여 검토하였다. 그 결과, 염화물 이온 농도차 3kg/m3 이하의 매크로셀 부식 환경에 대하여 Cr함유율 9% 이상의 Cr강재에서 방식성이 확인되었으며 특히, Cr함유율 11% 이상의 Cr강재에서 뛰어난 방식성이 입증되었다.