자동차 포핏밸브의 열 CVD법 TiC,N표면개질에 따른 트라이볼로지 특성 연구 KCI 등재
A Study on the Tribological Characteristics of Surface Modification by TiC,N of the Thermal CVD Method use to the Automotive Poppet Valve
pp.273-278
In order to determine the wear properties of CVD ceramic coatings, wear process was evaluated using the coated pin of Falex Tribosystem. Also, in order to determine the effects of coating material on wear process, TiC,N of thickness 5m∼6m coated by Thermal CVD method were applied. The wear property of TiC,N film, the higher the deposition temperature was, the closer the lattice parameter was to the amount of the standard power, and the grain size increased. According to the wear formation, under the control that there is on specific wear rate wear parameter and coating delamination, decrease with increasing sliding friction and when the coating delamination happened.