Although the structure of carbon nanotubes is important factor characterizing its properties, it is very difficult to control the structure of carbon nanotubes (MWNTs) and to predict the range of their diameter, which is the primary factor of MWNTs' physical properties. We tried to control the diameter of MWNTsby governing the feed injection temperature of floating catalyst method. The structure of MWNTs was influenced by the phase change of ferrocene fed as the catalyst,. The carbon nanotubes were very narrow at injection temperatures close to the sublimation pt. of ferrocene, in which most MWNTs had diameters in the range of 20~30 nm. At injection temperatures between the boiling pt. and melting pt. of ferrocene, the diameters became larger and had broad distribution. However, at injection temperatures higher than the boiling pt., the diameters became narrow again and had very uniform distribution.