Y2-xGdxO3:Eu, phosphors for plasma display panel(PDP), were prepared by Pechini method which use yttriun chloride, gadolinium chloride, and europium oxide as starting materials. This method is a different way to the synthesis of europium(Eu)-doped phosphors, and it consists of the formation of a polymeric resin obtained by polyesterification between metal chelate compounds and a polyfunctional alcohol. This needs lower temperature than solid-state synthetic method. The prepared Y2-xGdxO3:Eu phosphor particles had spherical shape and coherence. The luminescence intensity of Y2-xGdxO3:Eu phosphor particles increased according to the increase of gadolinium(Gd) content(to 0.8mol%), and Y1.2Gd0.8O3:Eu phosphors had the highest luminescence intensity under vacuum ultra violet(VUV) excitation. The optimum concentration of Eu in the phosphor and optimum calcination temperature was 3wt% and 1100℃. The prepared phosphors were consist of particle, and its size was between 100nm and 150nm. Among the different polyfunctional alcohols, diethylene glycol(DEG) improved the luminescence intensities of phosphors more than other additives. The Pechini method proved that it is demonstrated to be suitable for the synthesis of phosphors used in PDP.