논문 상세보기
pp.101-106
In this study, we successfully synthesized a nano-sized lanthanum-modified lead-titanate (PLT) powder with a perovskite structure using a high-energy mechanochemical process (MCP). In addition, the sintering behavior of synthesized PLT nanopowder was investigated and the sintering temperature that can make the full dense PLT specimen decreased to below by using powder as sintering agent. The pure PLT phase of perovskite structure was formed after MCP was conducted for 4 h and the average size of the particles was approximately 20 nm. After sintered at 1050 and , the relative density of PLT was about 93.84 and 95.78%, respectively. The density of PLT increased with adding and the specimen with the relative densitiy over 96% were fabricated below when 2 wt% of was added.