In this paper, we investigated the effect of the passivation stack with Al2O3, hydrogenated silicon nitride (SiNx:H) stack and Al2O3, silicon oxynitride (SiONx) stack in the n type bifacial solar cell on monocrystalline silicon. SiNx:H and SiONx films were deposited by plasma enhanced chemical vapor deposition on the Al2O3 thin film deposited by thermal atomic layer deposition. We focus on passivation properties of the two stack structure after laser ablation process in order to improve bifaciality of the cell. Our results showed SiNx:H with Al2O3 stack is 10 mV higher in implied open circuit voltage and 60 μs higher in minority carrier lifetime than SiONx with Al2O3 stack at Ni silicide formation temperature for 1.8% open area ratio. This can be explained by hydrogen passivation at the Al2O3/Si interface and Al2O3 layer of laser damaged area during annealing.

The purpose of this study was to investigate the appropriate water content in high omega-3 fatty acid Saury nuggets for the desirable texture. The approach was made with adding water and onion at various levels (0~20%). The main ingredients of the nuggets included saury mince, mild pizza cheese, and hydrated textured soy protein concentrate. The formulated products were molded (dia. 4.5, thickness 1.5 cm, 20 g), lightly battered, and flash fried for 4 min. at 160℃, and then frozen until tested. The frozen nuggets were cooked at 165℃ and subjected to sensory evaluations, texture analysis, and water content analysis during warming (0~60 min), as well as assessments of acid, peroxide, and TBA values (during 10 days of storage at 24℃). In the sensory evaluation, preference for texture was highest in the nuggets made with a 15% onion level. The hardness of the nuggets increased with increasing onion level. Moisture content was highest in the nuggets made with a 20% water level. Changes in hardness during warming (0~60 min) of Saury nuggets containing various water and onion levels increased in nuggets made with the 20% water level. The acid, peroxide, and TBA values of the Saury nuggets made with herbs and oriental herbal extracts decreased up to 10 days of storage.

The purpose of this study was to test the overall preference of Saury fishmeat nuggets. In order to remove off-flavor of Saury and to improve the sensory properties of Saury fishmeat nuggets, different concentrations of vegetables (onion, 0- 20%), different types of spices (ginger powder, white pepper powder, garlic powder) and different types of vegetables (onion & hot pepper, onion & pimento, mushroom & hot pepper, and mushroom & pimento) were added and the sensory properties were evaluated. Different types of herbs (Anthemis nobillis, Rosemarinus offcinalis L) and oriental herb (Angelica gigas Nakai, Acanthopanax sessiliflorus Seed) extracts were included as well to preserve the antioxidants in the nuggets after reheating. The main ingredients included saury mince, mild pizza cheese, hydrated textured soy protein, and egg white powder. The samples were molded (dia. 4.5 cm, thickness 1.5 cm, 20 g), lightly battered and fried for 2 min (2 time) at 160oC. The samples were then frozen, reheated (150oC, 20 min) and subjected to a sensory evaluation. In the sensory evaluation, Saury nuggets made with a vegetable concentration of 15% had the highest flavor, taste, and overall preference (V5). In addition, Saury nuggets made with 1 g of ginger powder and garlic powder scored the highest in the preference test (S2). Saury nuggets made with onion and pepper had the highest score in the preference test relative to all the other tested vegetables (SV1). Finally, in terms of the herb and oriental herb extracts, the nuggets made with the condensed extracts at a 1/20 ratio of Acanthopanax sessiliflorus Seed (AS) scored the highest in the preference test, since AS had the lowest offflavor taste.