Microstructure evolutions of thermosetting resin coating layers fabricated by electrostatic spray deposition (ESD) at various processing conditions were investigated. Two different typical polymer systems, a thermosetting phenol-formaldehyde resin and a thermoplastic polyvinylpyrrolidone (PVP), were employed for a comparative study. Precursor solutions of the phenol-formaldehyde resin and of the PVP were electro-sprayed on heated silicon substrates. Fundamental differences in the thermomechanical properties of the polymers resulted in distinct ways of microstructure evolution of the electro-sprayed polymer films. For the thermosetting polymer, phenol-formaldehyde resin, vertically aligned micro-rod structures developed when it was deposited by ESD under controlled processing conditions. Through extensive microstructure and thermal analyses, it was found that the vertically aligned micro-rod structures of phenol-formaldehyde resin were formed as a result of the rheological behavior of the thermosetting phenol-formaldehyde resin and the preferential landing phenomenon of the ESD method.

다양한 전자종이의 특징과 전자종이를 제작하였다. 전자종이를 제작 하여 전기 및 광학특성 평가를 하기위해 구동시스템과 광학시스템을 제작하 였다. 패널의 구동을 하기 위해서 주파수, 펄스 폭, 경사 등을 구현하기 위하 여 4채널의 구동장비를 제작하였으며, 패널에 적용 및 오실로스코프로 확인 하였다. 패널의 CIE, 반사율, 시야각을 측정하기 위하여 광학시스템을 구축하 였고, 광학시스템으로부터 데이터를 추출 할 수 있었다. 입자의 크기와 입자 충전의 layer의 관계를 알 수 있었으며, 이에 따른 광학특성 평가를 할 수 있었다.