The desulfurizers facility is cylindrical shape. To operate properly it needs nozzles cleaned, get rid of lime adhesion and sludge, repair the wear and corrosion of facility regularly. For this purpose, workers shall access the ceiling or vertical wall at high place. Ordinary scaffoldings such as steel pipe scaffolding or system scaffolding have been using so that workers can access them. With these ordinary scaffoldings, openings around cylindrical wall are inevitable which make workers can expose always to the risk of falling. The purpose of this study is to develop customized scaffolding to minimize the openings to prevent workers form falling during maintenance it. It consists of a hexagonal central tower and six trapezoidal outer towers. And the bracing among the towers have connected each other for self-standing and for maintaining the structure of towers. Span decks, the circumference footstools, steps, etc. are laid on each floor. The safety is reviewed by structural analysis and performance test. With this study, openings each floor of this scaffold are removed. The gap between the cylindrical wall and the edge of the work stage is approximately 100 mm. Therefore, we expect that workers can work safely and efficiently.

The very high temperature gas reactor (VHTR) is one of the next generation nuclear reactors for its safety, long-term stability, and proliferation-resistance. The high operating temperature of over 800˚C enables various applications with high energy efficiency. Heat is transferred from the primary helium loop to the secondary helium loop through the intermediate heat exchanger (IHX). The IHX material requires creep resistance, oxidation resistance, and corrosion resistance in a helium environment at high operating temperatures. A Ni-based superalloy such as Alloy 617 is considered as a primary candidate material for the intermediate heat exchanger. In this study, the microstructures of Alloy 617 crept in pure helium and air environments at 950˚C were observed. The rupture time in helium was shorter than that in air under small applied stresses. As the exposure time increased, the thickness of outer oxide layer of the specimens clearly increased but delaminated after a long creep time. The depth of the carbide-depleted zone was rather high in the specimens under high applied stress. The reason was elucidated by the comparison between the ruptured region and grip region of the samples. It is considered that decarburization caused by minor gas impurities in a helium environment caused the reduction in creep rupture time.

320˚C, 40%NaOH 용액의 autoclave에서 약 300wppm의 탄소를 함유하고 있는 15Cr-9Fe-balanced Ni 합금 판상시편에 대해 응력부식 저항성을 조사하였다. 부식시편은 700˚C, 100시간 동안의 열처리로 합금내부에 석출될 수 있는 가능한 한 많은 양의 크롬계 탄화물을 석출시킨 후, 다시 재용해에 의해 크롬계 탄화물의 형태를 조절하는 800˚C-950˚C범위의 최종열처리를 시행하고 급냉시킨 다음 U-자형으로 응력을 가하여 준비되었다. 최종열처리 온도가 올라감에 따라 시편들의 입계응력부식균열(IGSCC ) 전파속도는 900˚C까지는 거의 직선적으로 증가하다가 950˚C에서는 700˚C에서 얻은 값보다도 더 낮게 감소하였다. 즉, 크롬계 탄화물이 재용해되어 그 밀도가 감소함에 따라 IGSCC저항성이 감소하다가 완전히 재용해된 950˚C 열처리 조건에서 오히겨 가장 큰 IGSCC 저항성을 나타내었다. 이와같은 최조열처리 온도에 따른 니켈계 합금 600의 부식거동은 입계에 존재하는 크롬계탄화물의 형태변화 때문이 아니라 입계에서 탄소-크롬계 탄화물-크롬간의 상평형에 의해 이루어지는 탄소의 입계편석량이 크롬계탄화물이 존재할 때에는 열처리 온도에 따라 증가하다가 그것이 완전히 재용해 되었을 때 가장 낮아지기 때문인 것으로 생각된다.