The marine structures with sea water cooling system always expose to the oceanic atmosphere. Therefore, the protection of the equipments is very important. To investigate the effectiveness of advanced composite materials for the application in offshore environments, the tensile test, hardness test, undercutting property test, permeance test and the friction and wear test were carried out by using various applicable coating materials. The main results obtained can be summarized as follows; 1. The micro-hardness of the Archcoat 502B showed the highest value. 2. The coefficient of friction of the Rigspray coating at the speed of 2.21m/sec showed the lowest value, and that of the Archcoat 502B coating at 1.08m/sec and 0.18m/sec indicated the lowest values. 3. The wear mass at the speed of 0.18m/sec and 1.08m/sec in dry condition showed the smallest values. 4. The Archcoat 502B coating is fitted to the dynamic instruments in the range of low speed and middle speed. Rigspray coating is fitted to the dynamic instruments in the range of high speed. 5. The wear mass of five kinds of coating materials at the range of low speed was very small, and those of the Archcoat S02B, Archcoat 402B and Rigspray coating at high speed range were quitely smaller than those of the Modified Epoxy and Tar Epoxy.

플라즈마 화학기상증착법에 의해 증착된 저유전율 SiOF박막의 물성 안정화를 위하여 증착후 N2O플라즈마로 열처리함으로써 그 특성을 평가하였다. SiOF박막은 대기방치 및 열처리에 불안정한 성질을 가진다. SiOF 박막은 박막내의 F-Si-F 결합의 존재 때문에 흡습현상이 발생하며, 박막내의 F함량이 증가함에 따라 수분 흡수가 증가한다. 또한 열처리를 거치면서 F이 탈착되어 박막내의 F함량이 감소한다. N2O플라즈마 열처리는 표면에 얇은 SiON층을 형성시킴으로써 박막을 안정화시키는데 효과적이었다. 그러나 장시간의 N/sun 2/O플라즈마 열처리는 유전율을 크게 증가시킨다. 따라서 N2O플라즈마 열처리에 의한 유전율의 증가없이 물성을 안정화 시키기 위해서는, 대기방치나 열처리에 의한 안정화 효과를 유지하면서 N2O플라즈마 열처리에 의한 유전율의 증가를 최소화시킬 수 있는 공정의 확립이 필요하다.