Manganese dioxide (MnO2) is one of the most important cathode materials used in both aqueous and non-aqueous batteries. The MnO2 polymorph that is used for lithium primary batteries is synthesized either by electrolytic (EMD-MnO2) or chemical methods (CMD-MnO2). Commonly, electrolytic manganese dioxide (EMD) is used as a cathode mixture material for dry-cell batteries, such as a alkaline batteries, zinc-carbon batteries, rechargeable alkaline batteries, etc. The characteristics of lithium/manganese-dioxide primary cells fabricated with EMD-MnO2 powders as cathode were compared as a function of the parameters of a manufacturing process. The flexible primary cells were prepared with EMD-MnO2, active carbon, and poly vinylidene fluoride (PVDF) binder (10 wt.%) coated on an Al foil substrate. A cathode sheet with micro-porous showed a higher discharge capacity than a cathode sheet compacted by a press process. As the amount of EMD-MnO2 increased, the electrical conductivity decreased and the electrical capacity increased. The cell subjected to heat-treatment at 200˚C for 1 hr showed a high discharge capacity. The flexible primary cell made using the optimum conditions showed a capacity and an average voltage of 220 mAh/g and 2.8 V, respectively, at 437.5μA.

본 연구에서는 내열성 고분자인 폴리에테르술폰을 이용하여 전기방사의 방법으로 섬유 형태의 다공성 막을 제조하였다. 여기에 Nafion 용액을 함침 시켜 고분자 전해질 연료전지용 막을 제조하였다. 열중량 분석을 통해, 현재 고분자 전해질 막으로 상용화되어 널리 쓰이고 있는 Nafion 212보다 더 높은 열적 안정성을 갖는 것을 확인하였다. 주사전자현미경 측정을 통하여, 다공성의 폴리에테르술폰 막에 Nafion 용액이 수소이온 전도체로서 잘 함침 되어 있음을 확인할 수 있었다. AC impedance 측정 결과, 100°C 이하의 온도범위에는 수소 이온 전도도가 10 -2 S/cm로 나왔으며, 100°C 이상의 범위에서는 10 -3 S/cm의 값을 나타냈다. 0.6 V, 90°C의 조건에서 389 mA/㎠의 전류밀도를 나타내었다. Nafion 212 상용 막이 75°C에서 최대 성능을 나타내는데 반해, Nafion 용액을 함침시킨 폴리에테르술폰 막은 90°C에서 최대 성능을 갖는 것으로 나타났다.