본 연구에서는 다층 층간분리된 적층보의 자유진동해석을 수행하였다. 적층보에 존재하는 다층 층간분리가 고유진동수에 미치는 영향을 고찰하기 위해 층간분리단에서의 연속조건을 유도하고, 층간분리된 각각의 분할보의 경계에서 유도된 연속조건을 이용하여 진동수 방정식을 유도하였다. 이론해석결과의 검증을 위해 범용 프로그램을 이용한 유한요소해석을 수행하였으며, 서로 잘 부합됨을 보였다. 고유진동수 변화는 다층 층간분리의 크기와 위치 및 형태에 따라 변하였다. 얻어진 결과로부터 다층 층간분리가 적층보의 동적특성에 미치는 민감도와 층간분리의 위치와 크기를 탐지하는데 활용될 수 있는 가능성을 제시하였다.

In this study, it evaluate the impact resistance of UHPC by repeated impact. smooth steel fiber and polyvinyl alcohol fiber were reinforced in UHPC respectively. Overall, the impact resistance of the specimens reinforced with 0.4vol.% PVA fiber was high, and the crater diameter was small in specimens using 13mm fiber.

In this study, it evaluate the electromagnetic pulse shielding performance of fiber reinforced cement composite by Fiber type. Hooked-ended steel fiber, Smooth steel fiber and Amorphous metallic fiber were reinforced 2.0 vol.% in cement composites respectively. The electromagnetic pulse shielding performance was evaluated by MIL-STD-188-125-1.

As a result of evaluating the spalling properties using a restrained ring-type concrete specimen, in the case of rapid heating, the water vapor pressure rapidly rise and the surface spalling is repeated. In the case of low-speed heating, The water vapor pressure accumulated in the concrete exceeded the limit, and explosive spalling occurred inside.

Concrete has been recognized as a material which is resistant to the high temperature, but chemicophysical property of concrete is changed by the high temperature. So, mechanical properties of concrete may be reduced. Therefore, concrete is evaluated mechanical properties for safety inspection. However, research of ultrasonic pulse method is not much. Therefore, the purpose of this study is to Non-Destructive Test of 30, 70, 110MPa concrete exposed high temperature using ultrasonic pulse velocity.

Concrete has been recognized as a material which is resistant to the high temperature, but chemicophysical property of concrete is changed by the high temperature. So, mechanical properties of concrete may be reduced. Therefore, concrete is evaluated mechanical properties for safety inspection. However, research of ultrasonic pulse method is not much. Therefore, the purpose of this study is to Non-Destructive Test of 30, 70, 110MPa concrete exposed high temperature using ultrasonic pulse velocity.

LCC 분석은 비용평가만을 위한 개별적인 방법이 아닌 가치 개선을 위해 기능평가와 상호 연계되어 이루어지는 방법이다. 점차 LCC 분석의 정확성은 높아지고 있으나 비교적 최근에 개발․적용되어진 재료나 형식들에서는 공용기간이 확보되지 않아 여전히 유지관리 이력을 추정하기가 어려워 신뢰도가 떨어진다. 이런 배경으로 본 연구는 유지관리 프로파일을 설정하기 어려운 대안들에 대해서 기능적인 증감사항이 비용과 연계되어 분석되어지는 LCC 방법론을 제시하고자 한다. 최근 강상판 교면포장은 중차량과 교통량의 증가로 소성변형 등 문제점이 발생하여 기존의 포장을 대체할 수 있는 새로운 혼합물포장의 개발이 활발히 이루어지고 있다. SMA, Guss 및 PSMA 포장을 사례로 들어 대안 간에 비교된 성능척도가 상대평가계수로써 유지관리 프로파일 항목에 포함되어 LCC 분석이 이루어졌다.