Non-sintering cement was manufactured with briquette ash. Alkali activator for compression bodies used a NaOH solution. In order to apply alkali-activated briquette ash and the non-sintering cement to concrete, several experimental studies were performed. It was necessary to study the binder obtained by means of a substitute for the cement. This study concentrated on strength development according to the concentration of NaOH solution, the curing temperature, and the curing time. The highest compressive strength of compression bodies appeared as 353kgf/cm2 cured at 80˚C for 28 days. This result indicates that a higher curing temperature is needed to get a higher strength body. Also, geopolymerization was examined by SEM and XRD analysis after the curing of compression bodies. According to SEM and XRD, the main reaction product in the alkali activated briquette ash is aluminosilicate crystal.

CRT 브라운관 패널의 연마과정에서 배출되는 폐연마슬러지로부터 석류석 등의 연마재를 회수하고, 연마성능을 평가하였다. 재활용 부석과 석류석으로 연마한 유리의 평균표면거칠기값(Ra = 0.025μm, = 0.029μm)은 새 연마재로 연마한 유리에서의 값(Ra = 0.039μm, 0.031μm)보다 작았으며 표면의 선이나 홈도 적었다. 루즈의 경우 유리 파편이 혼입되어 연마재로 재활용하기에는 적합하지 않다. 본 기술을 이용하여 폐연마슬러지에 함유된 천연연마재 광물자원인 부석과 석류석을 회수한다면 CRT 유리 연마공정에서 재활용할 수 있고, 슬러지 매립으로 발생되는 처리비용과 환경오염문제를 줄일 수 있을 것이다.