In the flux used in the batch galvanizing process, the effect of the component ratio of NH₄Cl to ZnCl₂ on the microstructure, coating adhesion, and corrosion resistance of Zn-Mg-Al ternary alloy-coated steel is evaluated. Many defects such as cracks and bare spots are formed inside the Zn-Mg-Al coating layer during treatment with the flux composition generally used for Zn coating. Deterioration of the coating property is due to the formation of AlClx mixture generated by the reaction of Al element and chloride in the flux. The coatability of the Zn-Mg-Al alloy coating is improved by increasing the content of ZnCl2 in the flux to reduce the amount of chlorine reacting with Al while maintaining the flux effect and the coating adhesion is improved as the component ratio of NH4Cl to ZnCl2 decreases. Zn-Mg-Al alloy-coated steel products treated with the optimized flux composition of NH₄Cl•3ZnCl₂ show superior corrosion resistance compared to Zn-coated steel products, even with a coating weight of 60 %.

This paper investigated impact resistance capacity and failure mode of strengthened column with PROTECT (Poly-Resilience-Oriented hybrid TEChnology plaTe) panel by analytical study. PROTECT panel is the composite panel with two steel plates and nano-composite. In order to perform impact analysis, dynamic properties of concrete, steels and nano-composite were determined. Finite element analysis was performed with these properties under the drop-weight impact. From the FEA, different failure modes corresponding to different columns were derived.