Municipal solid wastes incinerator (MSWI) bottom ash and melting slag are used to prepare external panel for increasingthe recycling rate of them in this study. In case of external panel, the most important property is flexural strength. Becauseit is easily distorted by external force. Wasted glass fiber (below WGF) is used to increase the flexural strength of externalpanel. Flexural strength of prepared panel was 14.6MPa of the mixing ratio of 3.0wt% WGF. But compressive strengthwas decreased with the addition of WGF. Because L/S ratio has to be increased to enhance the workability at high additionamount of WGF. High liquid content hinders geopolymer formation. But compressive strength (about 20MPa) was notlow at this condition.

In this work, lightweight brick was prepared from aluminum dross, MS and MBA. Aluminum dross is discharged as by-product through the process of aluminum smelting. It can be used as foaming agent, because it produces hydrogen gas due to the reaction with alkali activator. In this study, the specific gravity and compressive strength of prepared brick was discussed with the addition of aluminum dross. Compressive strength, flexural strength and specific gravity was 36 MPa, 2.6 MPa and 1.48 at mixing ratio of 0.9wt% aluminum dross, respectively. The physical property of brick was debased with the addition of aluminum dross. Because the pore size was bigger in accordance with the addition of aluminum dross.