MoO3 metal oxide nanostructure was formed by hydrothermal synthesis, and a perovskite solar cell with an MoO3 hole transfer layer was fabricated and evaluated. The characteristics of the MoO3 thin film were analyzed according to the change of hydrothermal synthesis temperature in the range of 100 ℃ to 200 ℃ and mass ratio of AMT : nitric acid of 1 : 3 ~ 15 wt%. The influence on the photoelectric conversion efficiency of the solar cell was evaluated. Nanorod-shaped MoO3 thin films were formed in the temperature range of 150 ℃ to 200 ℃, and the chemical bonding and crystal structure of the thin films were analyzed. As the amount of nitric acid added increased, the thickness of the thin film decreased. As the thickness of the hole transfer layer decreased, the photoelectric conversion efficiency of the perovskite solar cell improved. The maximum photoelectric conversion efficiency of the perovskite solar cell having an MoO3 thin film was 4.69 % when the conditions of hydrothermal synthesis were 150 ℃ and mass ratio of AMT : nitric acid of 1 : 12 wt%.

1. 토양조건은 배수가 양호한 양토인 안룡통 보통답으로 칼륨을 제외하고는 우리나라 논토양의 평균 함량보다 낮은 토양이었다. 유기질비료로 처리구는 질소 표준시비량인 9kg/10a과 비슷한 N-P-K=8.45-4.89-9.24kg/10a를 시용한 반면 관행구는 표준시비량보다 많은 N-P-K=14.5-6.3-10.8kg/10a를 시용하였다. 2. 벼 수확 후 시험구 토양내 미생물상 분포를 조사한 결과 박테리아와 방선균의 수는 처리구에서 약간 높게 나타났고, 곰팡이의 수는 관행구에서 약간 높게 나타났다. 토양내 가수분해효소 생성미생물을 조사한 결과 호평벼 처리구에서 키틴분해미생물과 인산분해미생물 분포가 다소 높게 나타났다. 3. 병해충 발생정도는 전체적으로 처리구에서는 미미하게 발생하였다. 그러나 관행구에서 특히 호평벼에서 도복과 이삭도열병이, 잎집무늬마름병은 두 품종 공히 심하게 발생하였다. 혹명나방은 온누리에서 발생율이 높았는데 이는 질소 과다 시용으로 판단되었다. 4. 호평벼와 온누리 공히 관행구가 처리구에 비해 간장과 수장은 약간 길고, 주당수수는 많았다. 그러나 잎집무늬마름병 및 이삭도열병, 혹명나방 도복 등으로 등숙비율이 현저히 떨어졌다. 관행구는 천립중이 낮았으며 수량이 호평벼는 38%, 온누리는 13% 떨어졌다. 5. 병해충인 이삭도열병, 잎집무늬마름병, 혹명나방과 수량과의 관계에서 유의성이 높은 부의 상관관계가 나타났다. 6. 백미의 품질도 관행구에서 쇄립율의 증가로 완전미 비율은 낮고, 단백질함량이 높아 전반적인 품질 및 윤기치가 낮아졌다.