MoO3 metal oxide nanostructure was formed by hydrothermal synthesis, and a perovskite solar cell with an MoO3 hole transfer layer was fabricated and evaluated. The characteristics of the MoO3 thin film were analyzed according to the change of hydrothermal synthesis temperature in the range of 100 ℃ to 200 ℃ and mass ratio of AMT : nitric acid of 1 : 3 ~ 15 wt%. The influence on the photoelectric conversion efficiency of the solar cell was evaluated. Nanorod-shaped MoO3 thin films were formed in the temperature range of 150 ℃ to 200 ℃, and the chemical bonding and crystal structure of the thin films were analyzed. As the amount of nitric acid added increased, the thickness of the thin film decreased. As the thickness of the hole transfer layer decreased, the photoelectric conversion efficiency of the perovskite solar cell improved. The maximum photoelectric conversion efficiency of the perovskite solar cell having an MoO3 thin film was 4.69 % when the conditions of hydrothermal synthesis were 150 ℃ and mass ratio of AMT : nitric acid of 1 : 12 wt%.

질소산화물 등의 배출규제 강화로 인한 사용처의 확대로 SCR(선택적 촉매 환원) 촉매 수요가 증가하고 있으며, 이에 따라 폐촉매 발생량도 증가할 것으로 예상된다. 폐촉매는 지정폐기물로 분류되어 처리시에 비용이 발생하여, 물리적으로 재생하여 재사용 하거나 유가금속을 회수하는 방법으로 재활용하고 있다. 그러나 재생의 횟수가 제한적이고, 유가금속 회수는 비용이 고가이며 촉매의 85~90%를 차지하는 TiO2가 폐기된다는 문제점이 있다. 따라서, 본 연구에서는 SCR 촉매를 경제적이며 지속적으로 사용하기 위해 피독된 SCR 촉매 내 피독물질만 화학적으로 수세 및 정제하고 유가금속/TiO2의 함량을 높이는 최적의 세정 용매를 도출하는 촉매 재활성을 위한 기초연구를 수행하였다. 비교대상 촉매인 Poisoned 촉매를 5가지 세정용매로 화학적 처리결과, acetic acid 용매가 V2O5 1.19 wt%의 높은 함량과 57.6%의 높은 피독물질 제거효율을 나타내며 다른 산 처리 용매에 비해 촉매 재생성이 높은 것으로 분석되었다. 세정 용매의 농도와 세정 시간에 따른 V2O5 함량과 피독물질 제거효율에 미치는 영향을 알아보기 위해 각각 변수를 두어 실험을 진행하였다. 본 연구를 통해 0.1 N acetic acid로 처리한 촉매가 가장 높은 NOX전환율을 나타냈으며, 유가금속/TiO2 함량 또한 높게 나타나 본 연구 목표에 가장 적합한 세정용매로 판단되었다.