Because the damages of corrosion resulting from the chloride ion are very serious, many research studies have been performed to measure the penetration depth of the chloride ion. However, there is a problem with data selection obtained from collection during experiments. After careful study, it appears that the collected data are not conformed to a normal distribution. The result of this study will play a very important role, as a first step for the development and construction of a forecasting system to help determine a reliable service lifetime of marine structures.

해양 구조물은 일반 구조물과는 달리 구조물 속으로 염화물이 침투하기 때문에 시간이 지나면서 빠르게 부식을 하게 되고, 부식이 진행됨에 따라 구조물의 붕괴를 야기 시킨다. 그러므로 염화물의 침투 정도와 부식의 진행 상태를 예측할 수 있다면 사고 예방은 물론, 친환경적 해양 구조물이 될 수 있으리라 사료된다. 본 논문에서는 이러한 해양 구조물의 염화물 침투를 예측하고, 부식으로 인한 구조물 붕괴 및 사고를 예방하고자 Sample Design을 통하여 서로 조건이 다른 시험체를 해수에 잠식시키고, 일정기간이 지난 후 Data를 수집하였다. 수집된 Data는 정규분포(Normal Distribution)를 따르지 않는다는 사실을 알게 되었고, 수집된 데이터를 예측 시스템 구축에 활용하기 위한 준비 단계로서 데이터 선정의 타당성을 검토하기 위해 수명분포분석(Lifetime Distribution Analysis)을 실시한 뒤 그 결과를 제시하였다.

콘크리트의 수축현상은 체적 변화를 발생시키며 균열의 원인이 되어 구조물 내구성 및 안정성에 영향을 미친다. 콘크리트의 수축 에 영향을 미치는 요인은 매우 다양하며, 특히 골재는 시멘트 페이스트의 변형을 구속하여 수축 발생을 억제하기 때문에 골재의 특성은 수축 현상에서 중요하게 고려하여야 하는 부분이다. 한편, 골재 부족 현상으로 인해 천연 골재 대체재 개발 및 적용에 대한 연구가 다방면으로 진행되고 있으며 콘크리트용 골재로 사용 되는 재료도 점차 다양해지고 있다. 따라서 본 연구에서는 전기로 산화 슬래그를 굵은 골재로 사용한 콘크리 트의 수축 특성을 평가하기 위해 수축 실험을 진행하였으며, 실험 결과와 수축 예측 모델을 비교하여 기존 예측 모델의 적용성을 검토하였다. 실험 결과, 전기로 산화 슬래그를 굵은 골재로 사용함에 따라 수축량이 감소하는 결과가 나타났으며, 특히 자기수축 저감 효과가 크게 나타났다. 예측 모델과의 비교 시 건조수축과 자기수축 각각 GL2000 모델과 Tazawa 모델이 가장 유사한 예측값을 나타냈으나, 보다 정확한 예측을 위해서는 골재 및 혼화재의 물성을 고려할 수 있도록 보완이 필요한 것으로 판단된다.

고밀도 폐유리가 콘크리트를 포함하는 건설 재료로 사용 가능함이 밝혀짐에 따라 본 연구에서는 고밀도 폐유리를 잔골재로 적용한 RC 부재의 구조적 거동을 평가하고자 휨거동 실험을 수행하고 그 결과를 비선형 유한요소해석 결과와 비교 검토하였다. 그 결과, 고밀도 폐유 리를 잔골재로 사용하게 되면, 균열 개수가 감소하고 균열 간격 및 압괴 면적이 증가하였다. 또한, 고밀도 폐유리를 잔골재로 대체한 부재는 높은 처짐 단계에서 연성이 감소되었다. 이러한 이유로 천연골재를 사용한 부재와 동일한 방법의 해석 기법은 고밀도 폐유리를 잔골재로 대체한 부재의 휨거동에 대한 초기강성, 항복하중 및 최대하중을 제대로 예측하지 못하는 것으로 나타났으나, 압괴 진전에 따른 중립축 깊이가 감소하는 것을 해석적으로 구현하게 되면, 비선형 유한요소 해석 결과가 실험결과를 비교적 잘 예측하는 것으로 나타났다.

장기간의 사용수명을 요구하는 구조물의 건설재료인 콘크리트는 내구성이 우수하지만, 외부 환경적 요인에 의해 장기간 열화가 진행될 경우 성능 저하가 발생하기 때문에 이를 평가해야 한다. 따라서 본 연구에서는 콘크리트 부재를 제작하여 장기간 열화 환경에 노출시켜 콘크리트 부재의 휨거동 특성의 변화를 평가하고자 하였다. 그 결과, 장기 열화가 진행된 콘크리트의 압축강도는 감소하였으며, 항복 하중이 감소하고 그때의 처짐이 증가하였다. 또한, 광물질 혼화재를 혼입한 부재에서도 이와 동일한 경향이 나타났으나, 광물질 혼화재 종류에 따라 열화에 대한 저항성능 차이가 발생하는 것으로 나타났다.

실내 공기질의 오염이 점차 심각해짐에 따라 실내 공기질 개선을 위한 다양한 연구와 관련 제도가 점차 도입되고 있다. 그러나 실내 공기질 개선에 사용되는 기성 제품들은 높은 휘산성으로 인해 장기적인 포름알데히드 농도 저감에는 큰 효과를 나타내지 않고 있으며, 이에 따른 장기적인 포름알데히드의 방출에 대한 유효성 검증이 불분명한 실정이다. 따라서 본 연구에서는 콘크리트에 적용 가능한 실내 공기질 개선을 위한 기능성 물질을 선정하기 위하여 시공성능, 압축강도 및 포름알데히드 농도 변화를 측정하였으며, 그 결과 기능성 물질의 종류에 관계없이 모두 시공성능 및 압축강도를 일반 콘크리트(모르타르)와 동등 수준을 확보하였다. 또한 기능성 물질의 화학작용으로 인하여 포름알데히드의 농도 저감이 가능한 것으로 나타나 향후 실내 공기질 개선을 위해 기능성 물질의 사용이 가능할 것으로 사료된다.

본 연구에서는 굵은 골재 특성이 콘크리트 건조수축에 미치는 영향을 평가하기 위하여 높은 밀도를 가진 전기로 산화슬래그를 굵은 골재로 사용하여 콘크리트 건조수축 시험을 진행하였다. 실험 결과, 전기로 산화슬래그를 굵은 골재로 적용한 콘크리트의 경우 일반 골재를 사용한 콘크리트에 비해 건조수축 발생량이 저감되었으며, 이는 일반 골재에 비해 높은 밀도를 가진 전기로 산화슬래그의 물리적 특성에 기인한 것으로 사료된다.

본 연구에서는 일반 굵은골재와 더불어 전기로산화슬래그를 굵은골재로 대체하였을 때, 초기재령시기에 동결피해를 입은 콘크리트의 압축강도 특성을 평가하였다. 실험결과, 초기 재령시기에 동결 피해를 입었을 때, 전기로산화슬래그를 굵은골재로 혼입한 콘크리트의 경우에 압축강도 발현율이 일반 굵은골재를 사용한 콘크리트의 경우보다 더 감소하는 것으로 나타났다.

본 연구에서는 고 흡수성 폴리머의 입자형태와 혼입율에 따른 모르타르의 강도 특성을 조사하였다. 고 흡수성 폴리머의 수분 흡수·방출에 의한 내부양생 효과 검증을 위해 수중양생과 기중양생을 실시하여 강도 특성을 비교하였다. 실험결과에 따르면, 수중양생의 경우 입자형태와 혼입율에 따라 큰 차이를 나타내지 않았다. 그러나 기중양생의 경우 입자크기가 큰 고 흡수성 폴리머가 내부양생 효과로 인해 더 높은 강도 값을 나타내었다. 모르타르의 공극구조 분석을 통해 강도와의 상관관계에 대한 추가적인 분석이 필요하다.

본 연구에서는 고 흡수성 폴리머를 혼입한 콘크리트의 기초 물성을 평가하였다. 또한 콘크리트 내부의 SAP의 내부양생 효과를 확인하기 위해 표준양생과 봉함양생을 실시하였다. 실험결과, SAP의 혼입률이 증가함에 따라 슬럼프 감소율이 증가하였으며, 표면전기저항도 증가하였다. 재령 7일과 28일의 압축강도 측정결과, 표준양생을 실시한 경우 압축강도의 증감이 SAP의 종류와 혼입률에 관계없는 것으로 나타났으며, 봉함양생을 실시한 경우 SAP 혼입률에 따라 강도가 증가하였다.

In this study, the fundamental properties of concrete using industrial waste as aggregate were evaluated. The concrete specimens were prepared using the steel slag as coarse aggregate and heavyweight waste glass. It was found that when the electric arc furnace slag substitution ratio increased, air contents and density also increase. However, the slump is decreased with an increase in the substitution ratio of electric arc furnace slag.

In this study, chloride penetration resistance and electrical resistivity properties of concrete using industrial waste were evaluated. From the results, the chloride diffusion coefficient increases and electrical resistivity decreases when electric furnace slag is mixed. It is needed that the comparison of results with long-term because the electric furnace slag has a ferrous component.

In this study, they were evaluated that the fundamental properties of mortar using a superabsorbent polymer. From the results, the flow value tends to decrease as the SAP content increases, and the compressive strength shows no particular tendency. This is due to the difference in SAP absorption rate. Therefore, it is necessary to accurately measure the absorption rate depending on the type of SAP, and it is considered that addition of water should be depending on the absorption rate.

In this study, the compressive strength and elastic modulus of concrete mixed with electric furnace slag were evaluated. The concrete specimens were prepared using the steel slag as coarse aggregate and heavyweight waste glass as fine aggregate. From the results, compressive strength and the elastic modulus were improved with the addition of electric furnace slag.

In this paper, the flexural behavior of RC member recycled heavy weight waste glass as fine aggregate was evaluated by finite element analysis. From the results, the analytical results do not reflect the experimental results. This is because the stress-strain curve of the concrete specimen obtained from the compression test was used as the input data for the ABAQUS. Therefore, the ABAQUS, based on the experimental results of the stress-strain relationship of concrete, predicted the load-displacement relationship without considering the reduction in load capacity.

현재 많은 국가들이 천연자원이 고갈되는 문제에 직면해있고, 골재 공급이 어려운 상황이다. 이러한 상황을 고려하기 위하여 대체자원 개발을 위한 다양한 연구들이 수행되어왔다. 특히, 방사성 폐기물의 차폐를 위해 사용되는 고밀도 채움재는 많은 양의 골재를 필요로 한다. 또한, 채움재의 차폐 성능 개선을 위해서는 채움재의 밀도 증가가 요구된다. 따라서 밀도가 높은 산업폐자원의 중량콘크리트 골재로의 활용성을 확대하기 위한 기초 자료의 제공을 위해 본 연구가 수행되었다. 실험결과, OPC의 경우, 고밀도 폐유리에 의해 감소된 콘크리트의 강도는 제강슬래그를 사용해도 개선되지 않으나, 광물질 혼화재를 결합재로 사용하면 성능이 개선되었다. 따라서 고밀도 폐유리와 제강슬래그를 중량 콘크리트에 적용할 경우, 광물질 혼화재와 함께 사용하고, FA보다는 BFS를 사용하는 것이 바람직한 것으로 나타났다. 한편, 제강슬래그를 중량콘크리트의 골재로 대체할 경우, 제강슬래그의 높은 밀도로 인하여 탄성계수와 차폐성능의 개선이 가능할 것으로 판단된다.

최근 들어, 첨단산업의 발전으로 다양한 종류의 산업폐기물이 빠르게 발생하고 있다. 특히, 산업폐기물 중 중금속을 함유한 고밀도의 폐 브라운관 유리는 재처리 비용과 환경오염 문제로 인해 전량 매립‧처분되고 있다. 따라서 이러한 폐자원을 재활용하기 위한 기초 연구가 필요한 실정이다. 이에 본 연구에서는 중금속이 함유된 CRT 폐유리를 잔골재로 대체한 모르타르 시험체의 기초 물성과 방사선 차폐 성능을 분석하여 차폐 재료로의 활용성을 평가하였다. 연구 결과에 따르면 중금속을 함유한 CRT 폐유리를 잔골재로 대체한 시험체의 겉보기 밀도가 상승하였으며, 압축강도와 휨강도는 저하되는 현상을 나타냈다. 또한, 납 성분이 다량 함유된 폐유리 대체 시험체는 일반 모르타르 시험체보다 저에너지의 차폐 성능이 상승하는 효과를 보였으며, 122KeV·57Co 방사선원에 대해서는 일반 모르타르 시험체보다 2.5배 높은 선형감쇠계수를 나타냈다.

The heavyweight industrial waste was used as concrete ingredient instead of natural aggregate, however, design standard did not consider effects of heavyweight aggregate on flexural strength. Therefore, in this paper, correlation between compressive and flexural strength of concrete using industrial was compared. From the results, compressive strength and flexural strength decreased with industrial waste increasing. And, it was shown that the test results of flexural strength were higher than the predicted value from design standard.

A large amount of CRT waste has been generated due to the interruption of analog broadcasting in 2012. In particular, CRT glass has been pointed out as a cause of environmental pollution because it contains a large amount of heavy metals such as lead for electromagnetic shielding. In this study, the electrical resistivity of mortar specimen using CRT waste glass as fine aggregate was measured to investigate the relationship between electrical resistivity and shielding characteristics.

In this study, the properties of mortar substituted heavyweight waste glass were evaluated. From the results, the flow value and density increased as the substitution ratio of heavyweight waste glass increased, and compressive and flexural strength decreased.