A zinc-air battery consists of a zinc anode, an air cathode, an electrolyte, and a separator. The active material of the positive electrode is oxygen contained in the ambient air. Therefore, zinc-air batteries have an open cell configuration. The external condition is one of the main factors for zinc-air batteries. One of the most important external conditions is temperature. To confirm the effect of temperature on the electrochemical properties of zinc-air batteries, we perform various analyses under different temperatures. Under 60 oC condition, the zinc-air cell shows an 84.98 % self-discharge rate. In addition, high corrosion rate and electrolyte evaporation rate are achieved at 60 oC. Among the cells stored at various temperature conditions, the cell stored at 50 oC delivers the highest discharge capacity; it also shows the highest self-discharge rate (65.33 %). On the other hand, the cell stored at 30 oC shows only 2.28 % self-discharge rate.

본 연구에서는 기존의 염화물계 제설제인 염화칼슘(CaCl2) 및 염화나트륨(NaCl)과 비염화물계 제설제(NS 100) 초산화합물 함유 염화물 제설제(NS 40), 그리고 이들 제설제를 중량대비 일정비율로 혼합(NaCl 70%+CaCl2 30%, NS 40 70%+CaCl2 30%, NaCl 70%+NS 40 30%, NS 40 70%+NaCl 30%)하였을 때 제설성 능과 특성, 콘크리트의 동결융해저항성 및 강재의 부식에 미치는 영향을 실내시험을 통하여 비교 검토하였다. 이상의 시험결과를 바탕으로 동절기 구조물이 동해를 받을 수 있는 지역에서 염화물계 제설제를 사용할 경우 제설성능 및 효과, 강재의 부식성 콘크리트의 동결융해저항성 및 스켈링저항성에 미치는 영향을 고려해 볼 때 하나의 제석제를 사용하기 보다는 두가지 제설제를 적정 비율로 혼합하여 사용하는 것이 바람직한 방법임을 알 수 있었다. 혼합 사용시에는 제설성능 강재 및 콘크리트에 미치는 영향을 고려해 볼 때 NS40(70%)+염화칼슘(30%)이 가장 효과적인 것으로 나타났다.