PURPOSES: The objective of this study was to determine the optimum ratio of mix design, for a reclaimed asphalt pavement (RAP) content of 100%, for spray injection application. METHODS: A literature review revealed that spray injection is an efficient and cost-effective application for fixing small defective regions of an asphalt pavement. Rapid-setting polymer-modified asphalt mixtures prepared from two types of rapid-setting polymer asphalt emulsion were subjected to Marshall stability and wet track abrasion tests, in order to identify the optimum mix designs. RESULTS and CONCLUSIONS : Different mix designs of type A and type B emulsions were prepared using RAP and virgin aggregates, in order to compare the performance and determine the optimum mix design. The performance of mixtures prepared with RAP was superior to that of mixtures containing virgin aggregates. Moreover, for optimum ratio of the design, the binder content prepared from RAP was set to 1~2% lower than that consisting of virgin aggregates. Compared to their Type A counterparts, type B mixtures consisting of a reactive emulsion performed better in the Marshall stability and wet track abrasion tests. The initial results confirmed the advantages associated with using RAP for spray injection applications. Further studies will be performed to verify the difference in the optimum mix design and performance obtained in the lab-scale test and tests conducted at the job site by using the spray injection machine.

The effects of conventional rolling (CR) and differential speed rolling (DSR) on the microstructure and mechanical properties of a copper alloy sheet were investigated in detail. A copper alloy with thickness of 3 mm was rolled to a 50% reduction at ambient temperature without lubrication with a differential speed ratio of 2:1; sample was then annealed for 0.5h at various temperatures from 100 to 800˚C. Conventional rolling, in which the rolling speed of the upper and lower rolls is identical, was performed under the same rolling conditions. The shear strain introduced by the CR showed positive values at positions on the upper roll side and negative values at positions on the lower roll side. However, the shear strain showed a zero or positive value at all positions for the samples rolled by the DSR. The microstrucure and mechanical properties of the as-rolled copper alloy did not show very significant differences between the CR and DSR for the microstructure and mechanical properties. However, those properties showed very significant differences in the case of the annealed samples. The effects of rolling method on the microstructure and mechanical properties of the as-rolled and subsequently annealed materials are discussed in terms of the shear strain.