PURPOSES : In this study, a method for evaluating concrete bridge deck deterioration using three-dimensional (3D) ground penetrating radar (GPR) survey data and its in situ application are discussed. METHODS : Field surveys are conducted on two bridges in Yongsan-gu (Bridge A) and Seodaemun-gu (Bridge B) in Seoul using 3D GPR. The obtained survey data are used to calculate the dielectric constant map of each bridge using the extended common midpoint method. In addition, random points on both bridges are selected for the chloride content test in accordance with the KS F 2713 standard. The results from the dielectric constant map and chloride content test are compared. RESULTS : For Bridge A, it is discovered that the percentage of sections with a dielectric constant of 5.0 or less is 1.57%, whereas that above 5.0 is 98.43%; this indicates that the percentage of deteriorated sections for Bridge A is low. Meanwhile, for Bridge B, the dielectric constants calculated for the entire bridge exceed 5.0, which suggests no deterioration for Bridge B. Moreover, all the points selected for the chloride content test have less than 0.15% chloride content and have dielectric constants ranging from 5.0 to 7.0, which are favorable condition for the bridge deck. CONCLUSIONS : The analysis results of the dielectric constants of the concrete bridge deck obtained from the 3D GPR system are consistent with the actual chloride content results. Furthermore, additional verification of this method through field surveys on bridge sections with severe deterioration is highly recommended for future improvements.

PURPOSES: The objective of this study is to evaluate the properties of eco-friendly waterproofing materials for bridge decks. METHODS: Various waterproofing materials and construction methods that are widely used in Korea were evaluated. Then, the problems in field application were identified. In order to solve these problems, it is necessary to improve constructability and stability. Thus, the properties of heating waterproofing membranes and waterproofing systems using recycling additives were evaluated. In addition, a field test was conducted to ensure the construct-ability and stability. RESULTS AND CONCLUSIONS : Waterproofing materials were developed using waste tires and carbon black the results of the softening point test, tensile adhesion test, and shear adhesion test. A new sheet system, which consists of mesh and vinyl, was also determined from the sheet test. The properties of waterproofing materials were better than those developed under the "A Asphalt Concrete Pavement Construction Guidelines" according to the results of laboratory tests and the report of the authorized testing agency. Finally, the field test showed that the materials met quality standards. In future research, it will be necessary to conduct continuous field tests and follow-up inspections.

PURPOSES: The purpose of this study was to develop an urgent road-repair system and perform a field applicability test, as well as discover the optimum mix design for machine applications compared to the optimum mix design for lab applications. METHODS: According to reviews of the patent and developed equipment, self-propelled and mix-in-place equipment types are suitable for urgent pavement repair, e.g., potholes and cracks. The machine-application mix design was revised based on the optimum lab-test mix design, and the field application of a spray-injection system was performed on the job site. The mixture from the machine application and lab application was subjected to a wet-track abrasion test and a wheel-tracking test to calibrate the machine application. RESULTS and CONCLUSIONS : This study showed that the binder content could differ for the lab application and the machine application in the same setting. Based on the wet-track abrasion test result, the binder contents of the machine application exceeded the binder contents of the lab application by 1-1.5% on the same setting value. Moreover, the maximum dynamic stability value for the machine application showed 1% lower binder contents than the maximum lab-application value. Collectively, the results of the two different tests showed that the different sizes and operating methods of the machine and lab applications could affect the mix designs. Further studies will be performed to verify the bonding strength and monitor the field application.

국내의 고속국도와 일반국도는 특성상 넓은 지역을 관통하게 되어 해당지역에 생활권의 분할과 지역주민들의 소통, 이동간의 불편 등의 영향을 미치게 된다. 이로 인한 불편을 해소하고자 부체도로(附替道路)를 설계·시공하고 있다. 그러나 부체도로의 특성상 교통량이 기존 도로에 비해 현저히 낮은 수준으로 기존의 시멘트콘크리트 슬라브 20cm, 보조기층 20cm의 포장두께가 다소 과하다는 의견이 빈번하다. 이에 따라 본 연구에서는 부체도로의 교통량에 따른 등급을 설정하고 단면두께를 제안하였으며, 포장구조해석 프로그램을 통한 공용성 분석을 실시하였다. 전라북도 전주시 및 수도권의 부체도로 13개소 교통량 조사결과 일평균 약 40대로 국형포장설계법의 교통량 C1등급에 해당되는 교통량으로 조사되었다. 따라서 기존의 KPRP(한국형포장설계법) 카달로그 설계등급3의 포장두께가 다소 과다할 것으로 추정되며, 인근 공장에 의한 중차량하중이 발생하게 되는 것을 고려하여 기존의 한국형포장설계법의 포장두께를 수정하였다. 수정된 아스팔트포장 단면두께는 1∼100대 : C1(표층5cm·기층7cm·보조기층15cm), 101∼500대 : C2(5·8·17), 501∼1500대(중차량·농기계 주행고려구간) : C3(5·10·20)로 분류 하였다. 콘크리트포장과 아스팔트포장의 KPRP 비교·분석 시 콘크리트포장의 설계는 기준대비 균열율(%), 종단평탄성(m/km) 발생량이 비교적 낮은 값으로 나타났으며, 아스팔트포장의 경우 기층 10cm미만은 분석이 불가하여 C3단면을 분석한 결과 설계기준 값을 모두 만족하였다. 또한 KENLAYER(다층탄성해석 프로그램)와 ABAQUS(유한요소해석 프로그램)로 잔존수명 분석결과 콘크리트포장의 잔존수명은 사용 교통량에 비해 높은 값으로 나타났으며, 아스팔트포장의 경우 각 단면두께에 대해서 도로포장구조설계해설서(2011)의 층별 탄성계수를 사용하여 공용성을 분석한 결과 각각의 잔존수명이 유사하게 예측되었다. 세 가지 해석 프로그램의 분석결과 설계기준 충족 및 적정한 잔존수명을 나타내는 것으로 보아, 앞서 제안한 아스팔트 단면두께가 부체도로의 콘크리트포장 설계의 대안으로 적절하다고 판단된다. 따라서 부체도로 포장 설계 시 교통량, 중차량하중 등의 현장여건을 고려한 부체도로 설계를 반영한다면 기존 부체도로 포장에 비해 보다 합리적인 설계가 가능할 것으로 판단된다. 또한, 일반도로와 달리 단면두께가 최소화된 부체도로에 대한 공용석 분석 방안 및 도로포장에서 환경요인에 의한 파손유형 연구가 필요 할 것으로 판단된다

서울과 같은 도심지의 열악한 도로조건과 더불어 계속되는 유지보수용 절삭 덧씌우기로 인하여 일반 포장공법은 물론 기존에 공용성이 우수하다고 알려진 상용 개질 아스팔트 포장공법 또한 계획된 수명을 다하지 못하고 쉽게 파손되는 경향을 보이고 있으며, 도로의 통행안전에 위협을 가하는 요소로 작용하고 있다. 기존의 일반 및 개질 아스팔트 도로포장의 한계인 조기파손(골재탈리, 포트홀, 균열 등)과 기후변화로 인해 지속되는 고온현상에 의한 소성변형 등의 한계를 보이고 있다. 따라서, 본 연구에서는 국내 대표 개질 아스팔트 포장공법을 선정하였으며, 공법 간 물성비교 평가를 위해 배합설계를 실시한 후 재료 품질시험을 위한 아스팔트 혼합물을 제작하였다. 각 포장공법 별로 제작된 혼합물에 대한 공용성 평가를 위해 기본적인 물성 시험을 비롯하여 아스팔트 포장설계 시 재료의 물성을 평가하는 기준으로 적용되는 동탄성계수 측정과 더불어 내균열성 평가를 위한 SCB(Semi Circular Bending), 간접인장시험 등을 실시하였다. 시험에 사용된 혼합물은 일반적인 HMA와 소성변형 및 균열에 우수한 특성을 가지는 SMA를 대상으로 실시하였으며, 개질 아스팔트의 경우 PG 76-22의 아스팔트 바인더를 사용하여 각 포장공법의 공용성을 비교 평가하였다.