Graphite for the nuclear reactor is used to the moderator, reflector and supporter in which fuel rod inside of nuclear reactor. Recently, there are many researches has been performed on the various characteristics of nuclear graphite, however most of them are restricted to the structural and the mechanical properties. Therefore we focused on the thermal property of nuclear graphite. This study investigated the thermal emissivity following the oxidation degree of nuclear graphite with IG-11 used as a sample. IG-11 was oxidized to 6% and 11% in air at 5 l/min at 600˚C. The porosity and thermal emissivity of the sample were measured using a mercury porosimeter and by an IR method, respectively. The thermal emissivity of an oxidized sample was measured at 100˚C, 200˚C, 300˚C, 400˚C and 500˚C. The porosity of the oxidized samples was found to increase as the oxidation degree increased. The thermal emissivity increased as the oxidation degree increased, and the thermal emissivity decreased as the measured temperature increased. It was confirmed that the thermal emissivity of oxidized IG-11 is correlated with the porosity of the sample.

Mn-Mo-Ni 저합금강의 중성자 조사에 따른 기계적(미세경도, 인장, 샤피충격시험) 및 자기적(포화자화, 보자력, 잔류자화, Barkhausen Noise(BN)진폭, BN에너지) 성질 변화를 측정하여 이들의 상관관계를 고찰하였다. 기계적 성질시험 결과, 중성자 조사로 인하여 항복강도, 인장강도, 미세경도 및 천이온도(T41J)는 증가하였고 최대흡수에너지(USE)는 감소하였으며, 인장 시험의 경우 용접금속에서는 모재와 비교했을 때 큰 변화가 없었다. 자기적 성질을 측정한 결과, 잔류자화, BN진폭, BN에너지는 감소하였고 보자력은 급격히 증가하는 것으로 나타났다. 기계적.자기적 성질변화의 상관관계에서 자기적성질인 보자력 증가에 따라 천이온도, 항복강도, 경도는 증가하고 USE는 감소하였고, BN진폭의 경우는 보자력과 반대의 경향을 보였다. 본 실험에서 중성자조사로 인한 기계적.자기적 성질변화가 일관성 있는 상관관계가 있음을 확인하였고, 이들의 변화를 통해 조사손상을 평가하는 데 이용 가능하다.