The aim of this study was to investigate growth performance of growing-finishing pigs in response to high planes of nutrition. Seventy-two Yorkshire barrows weighing approximately 26 kg were randomly allotted to one of three planes of nutrition: ‘BASAL,’ ‘high’ (HI), and ‘extra-high’ (X-HI). BASAL, HI, and X-HI grower diets contained 1.15%, 1.25%, and 1.35% lysine and 3.48, 3.54, and 3.60 Mcal DE/kg, respectively; finisher diets had 1.10%, 1.10%, and 1.20% lysine and 3.43, 3.50, and 3.57 Mcal DE/kg, respectively. The animals were placed on the grower and finisher diets for 40 and 63 days, respectively, and slaughtered. Average daily gain, which did not differ among the three dietary groups during the grower phase, was greater (p<0.05) in the X-HI group than in the other two groups during the finisher phase (811, 862, and 842 g during the grower phase and 855, 884, and 953 g during the finisher phase for the BASAL, HI, and X-HI groups, respectively). Dressing percentage of the carcass was greater in the X-HI than in the other two groups, backfat thickness tending to be less in the X-HI group vs. BASAL (p=0.09). Results suggest that the growth rate of growing-finishing barrows could be increased by placing them on a high plane of nutrition.

진공증착법으로 제작한 V2O5 박막의 두께 및 결정성에 따른 전기변색 특성을 체계적으로 조사하였다. 증착된 박막은 노란색을 띄고 있었으며 140˚C 보다 높은 기판온도에서 증착된 V2O5 박막은 결정질로 낮은 기판온도에서 증착된 박막들은 비정질로 밝혀졌다. 리튬 이온 주입에 따른 V2O5 박막의 광 변조 특성 결과 V2O5 박막의 두께와 결정성에 관계없이 300~500nm 파장영역에서는 산화발색이 500~1100nm 파장영역에서는 환원 발색이 나타났다. 비정질과 결정질 Lix V2O5 박막의 optical band gap 에너지는 리튬 이온 주입양이 증가함에 따라 (x=0.0~0.6) 각각 0.75 [eV], 0.17 [eV]씩 높은 에너지쪽으로 이동하였다. 비정질 Lix V2O5 박막의 coloration efficiency는 근적외선 영역에서는 리튬 이온 주입과 박막두께에 따라 거의 변화가 없었으나 blue와 near-UV 영역에서는 absorption edge가 500nm 파장근처에서 높은 에너지 부근으로 이동됨으로 인하여, 박막두께가 증가하고 리튬 이온주입양이 감소할수록 coloration efficiency가 상당히 증가하는 것으로 나타났다. 그러나 결정질 Lix V2O5 박막의 경우 coloration efficiency는 전파장영역에서 리튬 이온 주입양과 박막두께에 거의 영향을 받지 않는 것으로 밝혀졌다.