TiN and CrN thin films are among the most used coatings in machine and tool steels. TiN and CrN are deposited by arc ion plating(AIP) method. The AIP method inhibits the reaction by depositing a hard, protective coating on the material surface. In this study, the characteristics of multi-layer(TiN/CrN/TiN(TCT), CrN/TiN/CrN(CTC)) are investigated. For comparison, TiN with the same thickness as the multilayer is formed as a single layer and analyzed. Thin films formed as multilayers are well stacked. The characteristics of micro hardness and corrosion resistance are better than those of single layer TiN. The TiN/CrN peak is confirmed because both TCT and CTC are formed of the same component(TiN, CrN), and the phase is first grown in the (111) direction, which is the growth direction. However, the adhesion and abrasion resistance of the multilayer films are somewhat lower.

In this study, the recently developed Al 2013 alloy was T8-tempered and, to improve the strength and corrosionresistance, slight amounts of Zr of 0.2 wt% and 0.5 wt%, respectively, were added and the mechanical properties were analyzed. For microstructure and precipitate analysis, OM observation, XRD analysis, and TEM analysis were performed, and for the mechanical property analysis, hardness and tensile strength tests were done. Also, in order to determine the corrosion rate according to the Zr content, a potentiodynamic polarization test was performed and the properties were compared and analyzed. The size of the precipitate varied with the content of Zr and was finest at Zr content of 0.2 wt%; it grew larger at 0.5 wt%, at which point the hardness value accordingly showed the same trend. On the other hand, as calculated from the aspect of chemical bonding among atoms, it was confirmed that the tensile strength and the corrosion-resistance increased with the same trend.