영활화혁발전소 보일러헤다 재질인 1Cr0.5Mo강의 파형에 따른 저주기 피로특성을 규명하고자 상온(298K) 및 고온(177K)의 삼각파와 사인파형 저주기 피로시험을 수행하였고 소성에너지법을 이용하여 파형에 따른 소성변형에너지와 피로수명과의 +관계를 분석하였다. 저주기 피로시 재료내부의 소성변형에너지를 히스테리시스루프의 면적으로 계산하여 구하였으며 이를통해 저주기 피로수명을 예측하였고 Coffin-Manson법 및 변형률분할법을 이용한 저주기 피로수명 결과와 서로 잘 일치하였다. 또한 상온 및 고온에서 피로반복수의 증가와 함께 재료가 반봅연화됨을 알 수 있었다.

The present study, a modified electrochemical treatment was applied to concrete to mitigate the leaching of alkali ions from concrete. The current ranged 500 mA/m2 and duration was 2weeks. Electrochemical treatment applied in concrete quantity of alkali ions leaching and the limit depth of concrete were decreased, through electrochemical treatment is very high inhibitory effect of the alkali ion is determined leaching.

In the attempt to predict life time in a concrete, some modified pore structure in concrete was taken accounted to a diffusion modelling. As a result, total length coming from MIP and LTM methods was somewhat inconsistent with corresponding value from profiling. The reason was assumed that overestimated surface chloride content and penetration length with unaccurate determination of continuous pores.

시멘트 내 6가 크롬은 피부질환이나 암을 유발할 수 있는 유해한 인체에 유해한 이온으로 잘 알려져 있다. 본 연구에서는 사람에게 영향을 주는 시멘트 내 6가 크롬의 정량적 분석을 하고자 시멘트 및 시멘트 경화체 내 6가 크롬의 고정화에 대해 평가하였다. 국내에서 생산되는 일반 포틀랜드 시멘트 3종과 플라이애쉬, 고로슬래그 미분말, 실리카퓸을 사용하여 수용성 및 산가용성 6가 크롬을 분광광도법으로 측정하였다. 측정결과, 시멘트 내 수용성 6가 크롬의 농도는 10.5-18.9 mg/kg-cement 범위였으며 혼화재료 내 수용성 6가 크롬의 양은 매우 적게 측정되었다. 시멘트 내 산가용성 6가 크롬의 농도는 172.4-318.2 mg/kg-cement 범위로 측정되었으며 수용성 6가 크롬에 비해 증가하였다. 그러나 크롬의 pH에 의존적인 용해 특성에 따라 용매의 pH가 저감된다고 하여 산가용성 6가 크롬의 농도가 항상 크게 측정되지는 않았다. 시멘트 수화 후 수용성 6가 크롬은 2.0 mg/kg-cement 정도로 감소하였으며 이는 크롬산-에트링게이트 생성에 의한 결과임을 확인할 수 있었다.

In a attempt to verify a reduction characteristic in leaching for hexavalent chromium from concrete structures, concrete specimens blended with Loess additive was exposed to sea environment followed by measuring the concentration of Hexavalent chromium from the specimens. Additional experiments with respect to basic properties of concrete with Loess additive were also performed. The entire results of experiments revealed that the reduction characteristic was predominant for concrete with Loess additive and basic properties of concrete with Loess additive were comparable to that of concrete with OPC.

Electrochemical treatments have been applied to many concrete structures. However, excessive current density degrades the bond strength by the change of microstructure at the steel-concrete interface. In this study, the optimal current density of electrochemical treatment without a influence on the bond strength could be derived from related literatures.

This study examined the setting time of Free-cement concrete and Ordinary Portland Cement(OPC). Alkali Activators(NaOH, KOH, CaOH2) were mixed when free-cement concrete was cast. Five different concentration levels of Alkali activator was used, ranging from 0.5%, 1.0%, 1.5%, 2.0%, and 3.0% by weight of binder.