Pt/C catalysts were prepared using black carbon (CB), and evaluated for their potential application as a catalyst of liquid-phase catalystic exchange for tritium treatment. CB was treated with 10% H2O2 solution for 0 and 2 hours at 105°C, Ethylene glycol and 40wt% Pt were added to the dried treated sample to prepare a Pt/C catalyst. The physical and chemical properties of the prepared catalysts were evaluated by BET, XRD, elemental analysis (EA), and TEM analyses. As a result of BET analysis, the surface area of CB without 10% H2O2 was 237.2 m2·g-1, and after treatment with 10% H2O2, it decreased to 181.2 m2·g-1 for 2 hours. However, the internal surface area increased, indicating the possibility that more Pt could be distributed inside the CB treated with 10% H2O2. In the XRD analysis results, the presence of Pt was confirmed by observing the Pt peak in the prepared Pt/C catalyst, and it was also observed through TEM analysis that Pt was evenly distributed within the CB. The elemental analysis (EA) results showed that the ratio of S and N decreased and the ratio of O increased with increasing 10% H2O2 treatment time. The H2O2 treated carbon supported Pt catalysts and polytetrafluoroethylene were then loaded together on a foamed nickel carrier to obtain hydrophobic catalysts. Our hydrophobic Pt catalyst using H2O2 treated black carbon are expected to be usefully used in the tritium treatment system.

Wide-area surface decontamination is essential during the sudden release of radioisotopes to the public, such as nuclear accidents or terrorist attacks. A spray coating composed of a reversible complex between poly (vinyl alcohol) (PVA) and phenylboronic acid-grafted poly (methyl vinyl ether-alt-mono-sodium maleate) (PBA–g–PMVE–SM) was developed to remove radioactive cesium from surfaces. The simultaneous spay of PVA and PBA–g–PMVE–SM aqueous polymer solutions containing Cs adsorbent to contaminated surfaces resulted in the spontaneous formation of a PBA–diol ester bond-based gel-like coating. The Cs adsorbent suspended in the gel-like coating selectively removed Cs-137 from the Cs-contaminated surface. The used gel-like coating were removed from surfaces by simple water rinsing. This recovery way has advantages compared with costly incineration to remove the organic materials for final disposal/storage of the radioactive waste. Thus, our spray coating is suitable for practical wide-area surface decontamination. In radioactive tests, the hydrogel containing Cs-adsorbent showed substantial Cs-137 removal efficiencies of 96.996% for painted cement and 63.404% for cement, which are 2.33 times better than the values for the commercial surface decontamination coating agent DeconGel.

A Partially hydrolyzed poly (vinyl acetate) (PHPVA)-borax complex-based gel-like coating was successfully developed for the decontamination of Simulated nuclear fallout (SFO) from surfaces. The sprayable coating was self-generated on the surface by borate-diol ester bonds after simultaneously mixing two solutions of borax and PHPVA. The SFO particles, synthesized at 1,200°C for melting, were glassy while some crystalline phases (e.g., SiO2 and Fe2O3) existed together. The SFO particles were fixed onto the Stainless steel (SS) substrate by dropping and evaporating water. for examination of the dust-removal performance of PHPVA-borax based coating. The dusts on the SS surface was successfully removed by casting the PHPVA-borax based coating within 1 minute, demonstrating the excellent dust-removal property of the PHPVA-borax based coating. The used PAB complex in wet state was recovered by using vacuum suction machine in short time. The solid-state PHPVA-borax based film was self-delaminated from the SS substrate after fully drying the used PHPVA-borax coating but this requires long period of time.