Molten chloride salts have received considerable research attention as potential nuclear fuel and coolant candidates for molten salt reactors. However, there are several challenges, especially for structural materials due to the selective dissolution of chromium (Cr) in the molten chloride salts environment. Understanding the compatibility of uranium (U), which is used as nuclear fuel in molten salt reactors, with Cr in molten chloride salts is critical for designing the molten salt reactor structure. Therefore, in this study, the cyclic voltammetry (CV) was used to investigate the electrochemical behaviors of U and Cr. The diffusion coefficients and formal potentials were obtained. The electrochemical properties of uranium and chromium were investigated by CV in molten NaCl-MgCl2 salt at 600°C. Tungsten rods for working and counter electrode, and Ag/AgCl for reference electrode were utilized in this experiment. UCl3 made from the chemical dissolution of U rods and CrCl2 (Sigma-Aldrich, 99.99%) were used. Diffusion coefficients (D) of U and Cr were calculated by measuring reduction peak current of U3+/U and Cr2+/Cr from CV curves and using the Berzins-Delahay equation; D (U3+/U) = 3.0×10-5 cm2s-1 and D (Cr2+/Cr) = 3.3×10-5 cm2s-1. The formal potentials were also calculated by using the reduction peak potential obtained from CV results; E0’ (U3+/U) = -1.173 V and E0’ (Cr2+/Cr) = -0.321 V. The ionization tendency was investigated by comparing each reduction peak potential. The reduction peak potential Ep,c was increasing order of Ep,c (U3+/U) < Ep,c (Cr2+/Cr) < Ep,c (U4+/U3+). It can be seen that in the presence of U4+ and Cr metals, the Cr in the alloy can dissolve into Cr2+, but in the presence of U3+ and Cr metals, the Cr in the alloy does not dissolve into Cr2+. By analyzing the CV curve, diffusion coefficients and formal standard potentials were obtained. The result of comparing reduction peak potentials suggests that the nuclear fuel using U4+ should be inhibited to prevent the selective dissolution of Cr.

This program aims to build a specialized and converged educational platform for the training of students in the back-end nuclear fuel cycle and cultivate integrated human resources encompassing majors, generations, and fields. To achieve this, we have established an infrastructure for integrated education and training in the radiochemistry and back-end nuclear fuel cycle and operated specialized educational courses linked with special lectures, experimental practices, and field trips. Firstly, to construct an integrated educational and training infrastructure for the back-end nuclear fuel cycle, we formed a committee of experts from both inside and outside the institution and built an advanced radiochemistry laboratory equipped with physical and chemical analysis instruments. Through a comprehensive educational program involving theory, experiments, and discussions, we have established an integrated curriculum across adjacent majors and interdisciplinary studies. We also operate short-term education and experimental training programs (e.g., summer and winter schools for the back-end nuclear fuel cycle). Secondly, the program has connected leading researchers domestically and internationally, as well as the next generation of scholars. The program offers long-term educational opportunities and internships targeting both undergraduate and graduate students. To support this, we continuously offer expert colloquiums and individual research internships. Through regular committee meetings and workshops, we focus on nurturing the integrated talents necessary for the back-end nuclear fuel cycle. Through this program, students from various fields are being trained as competent integrated human resources capable of addressing various issues in the back-end nuclear fuel cycle. It is expected that this will enable us to supply specialized technical personnel in the back-end nuclear field in line with mid-to-long-term demands.

One of the promising candidates for heat transfer fluid is molten chloride salts. They have been studied in various fields such as the electrolyte of pyroprocessing, the molten salt reactor coolant, and the energy storage system media. Main considerations for utilizing molten chloride salts are the compatibility of salts with structural materials. The corrosion behavior of structural materials in molten chloride salts must be understood to identify suitable materials against the corrosive environment. In this study, the corrosion behavior of a candidate structural material, Hastelloy N, in molten LiCl- KCl salt at 500°C were investigated by the electrochemical impedance spectroscopy (EIS) method. The sheet type of Hastelloy N was utilized as the working electrode in LiCl-KCl to measure the EIS data for 100 hours with 5 hours of time intervals. The EIS data were measured in the frequency range from 104 Hz to 10-2 Hz with the AC signal (amplitude = 20 mV) at open circuit potential. The capacitance semicircle observed in Nyquist plots for all periods indicates that charge-transfer controlled reactions occur. As the immersion time progresses, the radius of the semicircle in Nyquist plots and the impedance and phase angle in Bode plots decrease. These behaviors suggest a decreasing reaction resistance and the corrosion reactions are accelerated with the immersion time. The EIS data were fitted using the equivalent circuit to achieve quantitative results. Two capacitor-resistor components were considered due to the overlapped shape of two valleys in phase angle. The depressed shape of the semicircle in Nyquist plots led to the use of the constant phase element(Q) instead of the capacitor. Therefore, R(Q(R(QR))) circuit was selected to fit the EIS data. Fitting results show that the charge transfer resistance decreases dramatically within 1 day and then converges. The film resistance shows no clear trends, but the increase of the film admittance value indicates the decreased film thickness. Consequently, the film appears to exist like the oxide layer but it does not act as a protective layer. The real-time EIS data were measured in molten salt and provides the corrosion behavior over time. The corrosion mitigation strategy should consider that the corrosion of Hastelloy N accelerates over time and its intrinsic film cannot act as the protective layer. The next steps of this study are to evaluate other candidate structural materials and to demonstrate the presence of the film.

To investigate effects of starvation on physiological changes, stress response, and survival of cobitid loach (Misgurnus anguillicaudatus) exposed to sodium nitrite (NaNO2), a 4- week experiment was conducted. Fewer fish survived in the starved group than those in the fed group during the experiment. Starvation resulted in growth retardation, leading to differences in body length and body depth between fed and starved groups. The fed gorup continued to grow and remained in good condition. Blood chemical analysis (plasma cortisol and glucose) showed significant differences in stress response to nitrite exposure between fed and starved groups (p < 0.05). These results suggest that all parameters employed in this study to assess effects of starvation with NaNO2 stress are useful information for researching nutritional status in cobitid loach.

광나무(L. lucidum)는 ursolic acid와 oleanolic acid를 다량 포함하고 있다. 본 연구에서는 광나무 열매, 줄기, 잎 세 부위 추출물의 항주름 효능을 평가하였다. 광나무 추출물은 human skin fibroblasts에서 독성이 없을 뿐만 아니라 MMP-1과 MMP-2의 발현을 감소시키고 COL1A1의 발현을 증가시켰다. 이들 추출물은 모두 농도 의존적으로 COL1A1의 발현을 증가시켰으며 MMP-1과 MMP-2의 발현을 감소시켰다. 광나무 세 부위 추출물 가운데, 열매 부위에 가장 많은 양의 ursolic acid 와 oleanolic acid가 함유되어 있었으며 가장 강한 COL1A1 upregulating 효과와 MMP-1과 MMP-2 downregulating 효과를 나타냈다. 이처럼 항주름 효능을 보이는 광나무 열매 추출물은 기능성 화장품 소재로 개발될 수 있는 가능성이 있다.