In this study, we reported the microstructure and properties of Ag- contact materials fabricated by a controlled milling process with subsequent consolidation. The milled powders were consolidated to bulk samples using a magnetic pulsed compaction process. The nano-scale phases were distributed homogeneously in the Ag matrix after the consolidation. The relative density and hardness of the Ag- contact materials were 95~96% and 89~131 Hv, respectively.

Electro-Discharge Sintering (EDS) employs a high-voltage/high-current-density pulse of electrical energy, discharged from a capacitor bank, to instantaneously consolidate powders. In the present study, a single pulse of 0.57-1.1 kJ/0.45 g-atomized spherical powders in size range of 10~30 and consisting of -(Ti, Zr) and icosahedral phases were applied to examine the structural evolution of icosahedral phase during EDS. Structural investigation reveals that high electrical input energy facilitates complete decomposition of icosahedral phase into C14 laves and -(Ti, Zr) phases. Moreover, critical input energy inducing decomposition of the icosahedral phase during EDS depends on the size of the powder. Porous Ti and W compacts have been fabricated by EDS using rectangular and spherical powders upon various input energy at a constant capacitance of in order to verify influence of powder shape on microstructure of porous compacts. Besides, generated heat () during EDS, which is measured by an oscilloscope, is closely correlated with powder size.