Experiments with a URT-0.5 accelerator (0.5 MeV, 50 ns, 1 kW) generating a nanosecond electron beam for irradiation of silver nitrate in various liquid solutions (water and toluene) were performed with the aim of producing silver nanopowders. A radiochemical reaction allows making weakly agglomerated pure Ag powders with particles of 10-15 nm and 30-50 nm in size by irradiation in toluene and water respectively. The injection of the nanosecond electron beam energy to the solution is optimal. As the absorbed dose increases, the output of the radiochemical reaction does not grow, but more agglomerated powders are synthesized.

Trace analysis of Cd and Pb at surface modified thick film graphite electrode with Bi nanopowder has been carried out using square-wave anodic stripping voltammetry (SWASV) technique. Bi nanopowder synthesized by gas condensation (GC) method showed the size of nm with BET surface area, . For a strong adhesion of the Bi nanopowder onto the screen printed carbon paste electrode, nafion solution was added into Bi-containing suspension. From the SWASV, it was found that the Bi nanopowder electrode exhibited a well-defined responses relating to the oxidations of Cd and Pb. The current peak intensity increased with increasing concentration of Cd and Pb. From the linear relationship between Cd/Pb concentrations and peak current, the sensitivity of the Bi nanopowder electrode was quantitatively estimated. The detection limit of the electrode was estimated to be and for Cd and Pb, respectively, on the basis of the signal-to-noise characteristics (S/N=3) of the response for the solution under a 10 min accumulation.