This study investigated the surface pit corrosion of SS420J2 stainless steel accompanied by intergranular crack. To reveal the causes of surface pits and cracks, OM, SEM, and TEM analyses of the microstructures of the utilized SS420J2 were performed, as was simulated heat treatment. The intergranular cracks were found to have been induced by a grain boundary carbide of (Cr,Fe)23C6, which was identified by SEM/EDS and TEM diffraction analyses. The mechanism of grain boundary sensitization occurred at the position of the carbide, followed by its occurrence at the Cr depleted zone. The grain boundary carbide of (Cr,Fe)23C6 type precipitated during air cooling condition after a 1038 °C solid solution treatment. The carbide precipitate formation also accelerated at the band structure formed by cold working. Therefore, using manufacturing processes of cooling and cold working, it is difficult to protect SS420J2 stainless steel against surface pit corrosion. Several counter plans to fight pit corrosion by sensitization were suggested, involving alloying and manufacturing processes.

저장조에 위치한 사용후핵연료는 가혹한 원자로 조건에 의해 구조적 건전성이 와해되므로 외력에 취약하다. 따라서 운반 및 취급 중 사고 상황이 고려되어야 한다. 극단적인 경우, 핵연료 취급 중 사고로 인해 핵연료 저장조에서 핵연료집합체 낙하 가 발생할 수 있다. 이러한 사고 상황 하에서 연료봉 파손 등을 평가하기 위해서 수조에 충돌할 때 발생하는 충돌력을 분석 할 필요가 있다. 이는 핵연료가 수조 바닥에 충돌할 때의 속도를 입력으로 하여 평가될 수 있다. 연료봉이 핵연료 중량 및 부 피의 대부분을 차지하고 있으므로, 연료봉 다발은 수중 항력을 예측하는데 중요한 역할을 한다고 볼 수 있다. 본 연구에서는 3×3 의 짧은 연료봉 다발을 모델로 사용하여 수중에서 낙하할 때 받는 수력을 계산하였고, 이를 전산모사와의 비교를 통하 여 검증하였다. 본 방법론을 사용후핵연료 건전성 평가에 적용할 수 있을 것으로 기대된다.