In present work, amorphous TiCuNi powders were fabricated by mechanical alloying process. Amorphization and crystallization behaviors of the TiCuNi powders during high-energy ball milling and subsequent microstructure changes were studied by X-ray diffraction and transmission electron microscope. TEM samples were prepared by the focused ion beam technique. The morphology of powders prepared with different milling times was observed by field-emission scanning electron microscope and optical microscope. The powders developed a fine, layered, homogeneous structure with milling times. The crystallization behavior showed that glass transition, , onset crystallization, , and super cooled liquid range were 628, 755 and 127K, respectively. The as-prepared amorphous TiCuNi powders were consolidated by spark plasma sintering process. Full densified TiCuNi samples were successfully produced by the spark plasma sintering process. Crystallization of the MA powders happened during sintering at 733K.

본 연구에서는 인체 내에서 방사성핵종의 거동에 관하여 국제방사선방호위원회에서 권고한 최근 호흡기 모델, 소화기 모델 및 생체동역학 모델을 사용하여 생물학적분석 자료로부터 섭취량과 예탁유효선량을 평가하기 위한 BIDAS 프로그램을 개발하였다. 프로그램은 생물학적분석 자료를 관리하는 데이터베이스 모듈, 각 방사성 핵종에 대한 예측 생물학적분석 양을 내장하고 있는 모듈, 측정된 생물학적분석 양에 근거하여 급성 및 만성 피폭으로부터 섭취량과 선량을 평가하는 계산모듈 등으로 구성되어 있다. 본 논문은 프로그램의 특성과 검증결과에 대해 기술한다.

방사성핵종의 특성, 섭취형태 그리고 내부피폭 감시주기는 작업자의 방사성핵종 섭취량 및 내부피폭선량 평가 결과에 중요한 영향을 줄 수 있다. 따라서 방사성핵종이 흡입섭취 될 경우 섭취형태(급성 또는 만성) 및 내부피폭 감시주기에 따른 섭취량 평가 오차를 계산하였다. 섭취 핵종으로는 /I(Type F), Cs(Type F), U(Type M, Type S)를 고려하였고, 방사능입자크기(AMAD)는 1 와 5 를 고려하였다. 섭취형태에 따라 평가된 섭취량의 상대오차는 방사성핵종, 흡수형태 그리고 내부피폭 감시주기에 따라 달랐으나, 입자크기에 의한 영향은 거의 없었다. 섭취형태 가정에 따른 섭취량 평가 오차를 10% 미만으로 줄일 수 있는 내부피폭 최대감시주기는 /I(Type F)에 대해 60일, Cs(Type F)에 대해 180일, U(Type M)에 대해 90일, 그리고 U(Type S)에 대해 360일로 나타났다.