Effects of liquid phase and reinforcing particle morphology on the sintering of Al-6 wt％Cu-10 vol％ or SiC particles were studied in regards to densification, structure and transverse rupture properties. The Al-Cu liquid phase penetrated the boundaries between the aluminum matrix powders and the interfaces with reinforcing particles as well, indicating a good wettability to the powders. This enhanced the densification during sintering and the resulting strength and ductility. Since most of the copper added, however, was dissolved in the liquid phase and formed a brittle phase upon cooling rather than alloyed with the aluminum matrix, the strengthening effect by the copper was not fully realized. Reinforcing particles of agglomerate type were found less suitable for the liquid phase sintering than solid type particles. and SiC particles protluced little difference on the sintering behavior but their size had a large effect. Repressing of the sintered composites increased density and bending properties but caused debonding at the matrix-particle interfaces and also fracturing of the particles.

금속기지 복합물은 구조용 재료로서 매우 우수한 성질을 지니고 있어 광범위하게 연구되어져 왔다. Al2O3와 SiC는 그들의 우수한 기계적 특성 때문에 일반적인 보강재로서 사용되어져 왔다. 그러나 이들 세라믹 보강재는 비싼 재조 비용 때문에 특별한 목적을 위해서만 한정되어 사용되어져 왔다. 본 연구에서는 우리는 Al 합금기지 복합물에서 SHS법에 의해 합성된 Al2O3-SiC 분말의 보강재로서의 응용 가능성을 살펴보았다. 또한 Al2O3단섬유를 Al기지 하이브리드 복합물에 적용하기 위하여 합성된 분말과 함께 첨가하였다. 25vol% 강화재의 복합물을 제조하기 위하여 용탕단조법을 사용하였다. 미세구조와 결정구조는 SEM, OM 그리고 XRD로 관찰하였고 압축시험과 마모시험으로 기계적인 성질들을 조사하였다.