This study is to develop an export 1050MPa-class lightweight ductile iron castings Austempered control arm through the research process to obtain the following results. First, the structure of the optimal design Layout design and development of the component, and then achieve them through the Control Arm rigidity and optimal structure design and robust design of the focus areas of the expected stress Control Arm. Second, to develop a Control Arm reflects the high rigidity and high performance lightweight structures. Control Arm them developed to meet the design and rigidity as required by the consumer through the hollow, and to develop a process for the Core. Third, through optimum alloy composition and heat treatment methods will be derived to derive the amount of iron alloy (Cu, Ni, Mo) and Austempered heat treated and tempered condition. Fourth, through the development of optimum molding technology development component to develop the optimum ADI for the low-stiffness, high-rigidity component development, it attempts to develop a high-strength casting forming technology.

This research developed ultra-pressure pump main body by using ductile cast iron FCD500, conducted quantitative analysis on following phenomenon of flow or solidification processing in cast processing for improvement of cast device, after extracting model from cast concluded as follows by brinel hardness test. after selecting the ideal condition of cast and it applied to cast of real product shape, discovered the ideal filling processing under the condition that temperature of molten metal was between 1300℃ and 1280℃. and after finishing filling, solidification was commenced rapidly when percentage of solidification completion was between 40%~50%, at that moment, the termperature was measured 1100℃. moreover under the condition of temperature below 900℃, keeping temperature on the center of parts for a certain period of time brings stability of stabilization of heat in parts and organizational stabilization of ductile cast iron. As the results of the casting method design, it was that the ductile cast parts of pump main body was obtained as the maximum HB of 220 was recorded and good test results were achieved