PURPOSES : This study investigates the abrasion characteristics of coarse aggregate using the Los Angeles (L.A.) abrasion test and the accelerated polishing machine (APM) test. The coarse aggregates are randomly exposed on the surface of asphalt concrete pavements and on exposed aggregate concrete pavements. The exposed aggregates play a very important role in providing skid resistance. Therefore, the adequate abrasion resistance of coarse aggregate must be ensured to maintain the skid resistance during service life. In Korea, the LA abrasion test is conducted according to the KS F 2508 standard for the evaluation of the abrasion resistance of coarse aggregate. However, the road surface abrasion is caused by the friction between the tire and the road surface structure; hence, whether the LA abrasion test, which evaluates the abrasion caused by the impact of coarse aggregates and steel balls, can evaluate the road surface abrasion is questionable. A comparison and an analysis between the APM and LA abrasion tests were conducted herein to evaluate the road abrasion. An analysis was also performed to analyze whether the abrasion characteristics appeared depending on the type of coarse aggregate.
METHODS: The results of the APM and LA abrasion tests for various aggregate types were obtained through a series of experiments and literature reviews. The correlation between the LA abrasion loss and the PV data was derived. In addition, the influence of the aggregate type on the abrasion resistance was investigated.
RESULTS : An abrasion resistance database was established, and the relationship between the rock types and the abrasion resistance was statistically determined. The results showed that the PV was increased to 0.54 along with a 1% increasing rate of the LA abrasion loss with a 0.67 coefficient of determination. The abrasion resistance was also influenced by the aggregate type, which was found to be statistically significant.
CONCLUSIONS: A good relationship between the PV and the LA abrasion loss was obtained, allowing the use of the LA abrasion test (KS F 2508) alone, to reasonably evaluate the abrasion resistance of the exposed aggregate texture. The aggregate types were also found to have an impact on the abrasion resistance.
도로표지용 도료의 품질기준은 KS M 6080의 품질기준을 만족하는 제품들의 경우에도 시공 후 일정기간이 경과한 후에는 도료 자체의 부착력 문제로 교통량 증가에 따른 자동차 차륜에 의한 도료 자체의 마모 손실에 의하여 재귀반사 기능을 부여하는 유리알의 마모 및 탈리로 시인성이 급격히 저하되고 있다. 이에 따른 야간 교통 사고율 증가와 동시에 추가 교통 안전을 위한 부가 보완시공으로 안전시설 제비용이 직접비용으로 유발되고 있으며, 직접비용보다 추가공사로 인한 교통체증으로 사회간접 비용이 증가되고 있다. 특히, 차선의 품질 규격이 KS M 6080 제품에 만족한다 하더라도 빗물의 수막(水膜)에 의한 유리알의 굴절율 차로 재귀반사기능을 하는 차선 도료용 유리알의 기능을 발휘하지 못하여 운전자의 시인성은 열악함을 알 수 있다. 따라서, 국외에서 많이 사용되고 있는 마모성이 우수한 수용성 차선도료, 고성능 융착식 도료, 상온경화형 도료를 도입하여 성능을 비교 검토하였다. 본 연구에서는 차선재료의 내구성 향상을 위해 EN 1436규격에 의한 내마모성 시험을 수용성, 융착식, 상온경화형 도료에 실시하여, 재귀반사도 성능이 우수한 차선재료의 적용 가능성을 확인하였다.
As a result of abrasion resistance test of decoration wood-based flooring board laminated with PVC on plywood, compared to the flooring board laminated with general HPL surface decoration materials, it was available to secure far higher abrasion resistance. It seems to contribute to secure initial durability and maintenance of decoration wood-based flooring board as an important means, and it might be available for saving repair and maintenance costs due to flooring board issues.