Aluminum material, which has excellent corrosion resistance, durability, and light weight, is widely used in the field of shipbuilding, and welding is an essential technology in shipbuilding. currently, welding is efficiently used to assemble structures of various sizes in the shipbuilding process, but aluminum is a very sensitive material at high temperatures and in a molten state, so appropriate process control is essential. research on aluminum welding has been continuously conducted, but most of the research is on the butt welding method. therefore, in this study fillet welding experiments, which are essentially applied to the internal structure of aluminum ships, were performed and the correlation between welding beads and process variables was identified. for the welding experiment GMA fillet welding was performed on Al5083 material used in the shipbuilding industry, and the influence of the process variable was confirmed by analyzing the correlation through the analysis of the etched fillet weld bead cross section for the test result according to the process variable.

The bead geometry according to the welding conditions was analyzed through the laser fillet welding experiment of 9% Ni steel, and the relationship between the shear strength and the five bead geometry measured by selecting the main bead geometry of the fillet weld was analyzed. Among the welding conditions, the welding conditions that directly affect the penetration depth are welding speed and laser power, and the working angle and beam position have a great influence on the formation of leg of vertical and horizontal members. The bead shape, which greatly affects the shear strength, is the horizontal member length, neck thickness, and weld length, and has a proportional relationship with the shear strength. As a result of confirming the relationship between shear strength and bead shape through the derivation of the trend line, it was confirmed that the length of the vertical member, whose R2 value was 0.92, was most closely related to the shear strength.

Natural gas is the most realistic fuel among eco-friendly fuels. Natural gas production is limited, and in Korea, it is supplied and utilized in the form of liquefied natural gas (LNG). In the case of LNG, the vaporization point is 163 degrees below zero, so ordinary metal cannot be used due to its brittleness. The International Maritime Organization (IMO) defines metals that can be used in the IGC Code, and is used for storage containers, transportation containers, etc. based on the metals. Welding is essential in the manufacture of large structures such as LNG storage tanks. In this study, weldability studies related to cryogenic materials were conducted. In Part I of this study, high-manganese steel and part II were studied for two types of stainless steel (STS304L, STS316L), and in Part III, aluminum (AL5083). During laser welding, the shape of the Bead on Plate (BOP) was analyzed, and a total of nine cases were analyzed using laser power and welding speed as variables. It was confirmed that the penetration and the width of the welding width were linearly proportional to the amount of heat input. Based on this study, it is possible to conduct a follow-up study to find the optimal welding conditions for butt welding and fillet welding.

As the part of efforts to respond to the environmental pollution, the demand for clean energy is increasing. Natural gas is one of the most realistic alternatives, and interest in the storage and transportation containers to utilize the natural gas is growing. The production area of ​​natural gas is limited, and in Korea, it is imported in the form of liquefied natural gas. LNG is a cryogenic state with a vaporization point of -163°C, so the ordinary metal cannot be used due to its brittleness. The international maritime organization (IMO) defines the metals that can handle LNG in the IGC Code, and the research is ongoing. This study was a preliminary study to check the weldability of related metals and confirmed the shape of bead on plate (BOP) during the laser welding for each material. In part I, a study was conducted on the high manganese steel, and in part II, a study was conducted on the materials of STS304L and STS316L among the stainless steel. Based on this study, it can be used as an optimal welding condition for the butt and fillet welding.

As demand for eco-friendly energy increases, demand for natural gas and Liquefied natural gas (LNG) storage technologies continues to increase. LNG is a cryogenic environment with a temperature of -163°C, so ordinary metals cannot be used due to brittleness. Accordingly, IGC Code designates the cryogenic materials such as Invar, STS304L, Al5083-0, and High Manganese Steel. For fabricating those materials, research on welding possibility is the most important. Thus this study focused on the possibility of laser welding of the cryogenic materials. The weldability of High Manganese Steel was researched in this paper, the shape and the dimensions of the beads after bead on plate (BOP) welding were observed. The experiment was conducted on a total of 25 cases with laser power and welding speed of 5 cases each, and the width, height, and penetration of the beads were confirmed. It was confirmed that the paramenter of bead increased linearly with the laser power, and the paramenters of bead increased linearly with decreasing welding speed. Based on this study, high manganese steel can be applied in various industries by applying it to butt welding.