차량의 동적하중이 도로상에 작용하는 위치를 계측하기 위한 원더링 계측용 사선센서의 적정 설치각도를 제안하였다. 이를 위해서 테이프스위치 센서를 이용하여 원더링 계측용 장비를 개발하였고, 개발된 장비와 실험차량을 이용하여 평가용 자료를 수집하였다. 수집자료 분석 결과, 사선센서의 설치각도가 커질수록 원더링 수집자료의 오차가 감소하였고, 이러한 오차의 감소는 통계적으로도 의미가 있는 것으로 분석되었다. 그러나 사선센서를 30˚ 이상으로 설치할 경우, 탠덤축의 제원상의 이유로 인해 오류자료가 수집되는 것을 확인할 수 있었다. 따라서 본 연구에서는 국내 차량제원 등을 종합하여 원더링 계측용 사선센서의 적정 설치각도를 20˚~25˚로 제안하였다.

In this thesis, using the 400 series ferrite stainless steel such as 434LD2 which are furter excellent then the existing ferric products in mechanical characteristics, and experiment has been conducted on corrosion resistance of sensor ring. The results are following. 1. The products before sintering are much more corrodible in the condition of spray test of salt water and ammonia than humidity and nitrogen condition. 2. 434LD2 ferrite stainless steel has shown a good corrosion resistance without an addition surface treatment. thus the decreasing production process has been obtained. 3. As hardness value of HRB 80 and tensile test, 434LD2 ferrite stainless steel with show a good endurance when it is combined to constant velocity joint (c/v joint), and has a good hardness properties endurable to sand and pebble impact.

ABS sensor ring has been manufactured by powder metallurgy (P/M) method using 400 series ferrite stainless steel. The results are following. It is supposedly sufficient to use for control computer due to good experimental results of magnetic characteristics. Compared with sensor ring made by iron, 400 series ferrite stainless steel has shown a good corrosion resistance without an addition surface treatment. Thus the decreasing production process has been obtained. As a result mechanical characteristics of hardness and tensile test, 400 series ferrite stainless steel shown a good endurance when it is combined to constant velocity joint(C/V), and has a good hardness properties endurable to sand and pebble impact. The products before sintering are much more corrodible in the condition of spray test of salt water and ammonia than humidity and nitrogen condition.

In this paper, sensor ring for antilock brake system was studied using the 400 series ferrite stainless steel powder. Because of more excellent corrosion resistance and mechanical characteristics than iron, sensor ring has been manufactured by P/M(Powder Metallurgy) method 400 series ferrite stainless steel. the results are following. 1, Compared with sensor ring made by iron, 400 series ferrite stainless steel has shown a good corrosion resistance without an addition surface treatment. thus the decreasing production process has been obtained. 2. The products before sintering are much more corrodible in the condition of spray test of salt water and ammonia than humidity and nitrogen condition.