This study investigates construction practices for expansion joint using fiber net. After completion of underpass construction of concrete action by the ambient temperature, vehicle vibration and cyclic load due to cracking of asphalt layer expansion joint can penetrate broken asphalt and concrete pavement rapidly destroy the pavement.

In the nuclear power plant, the steel or polymer liner plates are adopted to prohibit the inner concrete surface from contacting with gas or liquid materials. If there is an accident, the plate may be damaged, and, in this case, concrete shall have the final responsibility to safety requirements. In this paper, an experimental research was carried out to investigate the effects of construction joint and wet and loading conditions on the permeability of concrete. The test results showed that, under a construction joint in the wet condition, leakage of gas pressure has been started from 1 kg/cm2. However, when there are no construction joints, it is initiated from 2 kg/cm2. In addition, under the air dried and unloading condition, regardless of with or without the presence of the construction joint, since the gas passage that exist in concrete is constant, leakage has a constant tendency to increase. Finally, under the loading condition, as described in Reference 1, since leakage is inversely proportional to the thickness of the wall, and, considering the wall thickness of the actual plant, it is found that there will not be no problem in the sealing of the gas.

A series of tests on the bond characteristics between new and old concrete were carried out. Main test variables are type and amount of mineral admixtures, treatment method of the interface and type of waterstops. The test results showed a slightly increased bond strength when applying mineral admixtures and the interface was treated rough and dry.

기존 고속철도 자갈궤도구간에서는 궤도 비틀림 현상이 발생하여 안전 위협, 승차감 저하, 유지 및 보수 비용증가, 유지 및 보수 작업으로 인한 열차운행 지연 등의 문제점이 발생하고 있는 실정이다. 궤도구조 개량공사는 열차차단 시간 내에 공사를 완료하고 공사 후 궤도에 대한 구조적인 안전성도 확보해야 한다. 이를 해결하기 위하여 열차차단 시간 내에 궤도 구조를 개량 할 수 있는 급속경화궤도 기술개발에 대한 연구가 진행되고 있다. 급속 경화궤도는 일반 자갈도상궤도를 콘크리트 슬래브화 시키는 공법이며 기존의 콘크리트궤도와 상이하게 철근이 사용되지 않고 자갈과 초속경 모르타르로 구성되어있다. 국내 고속철도에서 콘크리트경화궤도의 시공이음부에서 구조적 문제가 다수 발생하고 있다. 본 연구는 급속경화궤도 시공 시 발생하는 시공이음매에 대한 보강방안으로 자갈맞물림(Aggregate interlock), Dowel bar, Dowel plate, 지오그리드로 매개 변수화하여 급속경화궤도 시공이음부 보강구조의 성능 검증 실험을 수행한다. 이를 통해 급속경화궤도 슬래브 간에 하중전달효율을 분석하고 급속경화궤도 시공에 적합한 방안을 도출하고자 한다.