With the increasing number of aging buildings across Korea, emerging maintenance technologies have surged. One such technology is the non-contact detection of concrete cracks via thermal images. This study aims to develop a technique that can accurately predict the depth of a crack by analyzing the temperature difference between the crack part and the normal part in the thermal image of the concrete. The research obtained temperature data through thermal imaging experiments and constructed a big data set including outdoor variables such as air temperature, illumination, and humidity that can influence temperature differences. Based on the collected data, the team designed an algorithm for learning and predicting the crack depth using machine learning. Initially, standardized crack specimens were used in experiments, and the big data was updated by specimens similar to actual cracks. Finally, a crack depth prediction technology was implemented using five regression analysis algorithms for approximately 24,000 data points. To confirm the practicality of the development technique, crack simulators with various shapes were added to the study.

In recently, the method estimated construction's defeat using the infrared thermography was prefer to method of new repair and estimate as a good point that simple of application and save labor, what is more economic than other techniques and can reduce need time. The purpose of this study is to develope the technique to measure the corrosion of reinforcing bars using the infrared thermal photography graphic data. In this page, the former final purpose establishment that galvanic corrosion method of reinforced bars and infrared thermography system, and studied trend of thermography and photography graphic data by parameters of corrosion of specimens, atmosphere temperature, concrete cover depth etc.

현재 정부에서는 폐자원 에너지의 회수･사용을 촉진하기 위해 정책적인 움직임을 보이고 있다. 폐기물 소각시설의 소각열에너지 회수･사용률 산정방법이 2015년에 확정되었고, 이를 반영한 자원순환기본법이 2018년 1월 1일부터 시행될 계획이다. 이에 따라, 국내 폐기물 소각시설의 에너지 회수･사용률을 증가시키기 위해 열에너지 회수를 통한 전기나 열원 생산의 효율을 측정하고 평가하는 것이 필요하다. 폐기물 소각시설 공정에서의 방열손실은 열에너지 회수의 효율을 저하시키는 원인 중 한가지이다. 이를 평가하기 위하여 소각시설의 벽면온도를 측정하여야 하며, 현재의 소각시설 벽면 온도 측정 방법은 환경부 고시 ‘폐기물 처리시설의 세부검사방법에 관한 규정’의 별표1 ‘폐기물 소각시설의 세부 검사방법’에 따른 지점측정 방식이다. 하지만 지점측정 방식의 온도 측정은 접촉식 온도계를 이용한 측정법으로, 대상의 접촉 지점에 따라 온도가 다르게 측정될 수 있으며 대상 시설의 평균 표면온도를 정확하게 측정하는 것에 한계를 가진다. 적외선 열화상 카메라는 대상의 넓은 면적을 동시에 촬영하여 온도를 측정하는 방식으로, 시설의 평균 표면온도를 비교적 정확하게 측정할 수 있다. 따라서 본 연구에서는 실제 가동 중인 폐기물 소각시설의 벽면 온도를 비접촉 온도 측정 방식의 적외선 열화상 카메라를 이용하여 측정하고, 기존에 수행되었던 연구를 통해 정립된 방열손실 산정식을 이용하여 방열손실을 계산하였다. 또한 폐기물의 소각 온도, 소각 용량, 소각로 표면적 크기 등 여러 가지 요인에 의한 방열손실을 고려하기 위하여 소각시설의 입열과 출열 항목을 측정하여 투입된 에너지 대비 손실량인 방열손실률을 산정하여 평가하였다.

The Infrared-Thermography Technique is widely used for nondestructive evaluation (NDE) of structures due to its convenience. Particularly, various techniques have been tried to detect imperfections such as surface defects and welding defects of steel structures. This paper is a part of a study to detect defects in weld zone in steel structures using Infrared Thermography techniques. Finally, defects were detected by comparing infrared thermal image and surface temperature data of defected area with healthy area.

Recently, domestic waste policy has focused on resource circulation. In accordance with Article 3, Paragraph 2 of the “Enforcement Rules of Wastes Control Act”, which is targeted at waste incineration facilities, we established and announced methods for calculating the recovery and utilization rates of incineration-sourced heat in 2015. The lower heating value is important to energy recovery and utilization rate calculations. Hence, the lower heating values of the waste incineration facilities were estimated using the thermal method from KS B 6205. Heat loss decreases the heat recovery efficiency, and should be measured and evaluated. The surface temperatures of the incinerator and boiler are required to determine heat loss. Presently, the contact point temperature method is used to measure the surface temperature. It is difficult to apply this method to the average surface temperature of an incineration facility. In this study, 20 Korean waste incineration facilities were selected for heat loss estimates based on waste incineration temperature, incinerator type, and incineration capacity. Infrared thermal cameras were used to measure the surface temperatures of the waste incineration facilities.

‘전국 폐기물 발생 및 처리현황’(환경부, 2014)에 따르면, 국내의 전국 폐기물 총 발생량은 매년 증가하는 추세이다. 건설 폐기물을 포함한 ‘14년도 총 폐기물 발생량은 388,486톤/일에 달하며, 지정폐기물을 포함하면 폐기물 발생량은 더 증가한다. 이렇게 발생한 폐기물은 매립, 소각, 재활용, 해역배출로 처리되었다. 하지만 국내의 육상 폐기물 해역배출은 런던협약에 ‘16년부터는 전면 금지되었으며, 매립과 재활용을 통한 폐기물의 처리는 한계가 있다. 지속적으로 발생량이 증가하는 폐기물의 처리와 지정폐기물, 재활용 금지 및 제한대상 폐기물을 처리하기 위하여 폐기물의 소각처리가 필수적으로 요구된다. 국내에서는 정책적으로 폐기물 소각시설의 폐자원에너지 회수와 사용에 대해 집중하고 있으며, 2015년에 폐기물 소각시설의 소각열에너지 회수･사용률 산정방법을 확정하여 2018년 1월 1일부터 자원순환기본법을 통해 시행할 것을 예고하였다. 사업장폐기물 소각시설의 소각열에너지 회수･사용률 산정방법에 따르면 열정산법을 이용해 입열과 출열을 산출하여 소각시설의 효율을 계산한다. 소각로의 방열손실은 에너지의 회수 효율을 낮추는 출열 항목 중 한가지로 각 시설마다 측정하여 평가되어야 한다. 현재 방열손실 평가를 위한 소각로의 벽면 온도 측정은 지점측정법을 이용하여 실측되고 있다. 하지만 접촉식 온도 측정은 대상의 접촉 지점마다 온도가 다르게 측정 될 수 있으므로 대상 시설의 평균 표면온도를 정확하게 측정하는 것이 어렵다. 비접촉 방식으로 온도를 측정하는 적외선 열화상 카메라는 넓은 면적의 온도를 동시에 측정 가능하며 대상 시설의 평균 온도를 비교적 정확하게 측정 할 수 있다. 따라서 본 연구에서는 폐기물 소각시설의 출열 항목 중 방열손실의 측정 및 평가를 위해 적외선 열화상 카메라를 이용하였으며, 소각로 표면 온도 측정방법과 소각시설의 방열손실 산정 방법을 정립하였다.

Existing nondestructive test methods used to measure reinforcement corrosion is based on qualitative measurement of corrosion, and it has many difficulties of use because many equipment and measurement stages are required for application at actual sites. Accordingly, this study was conducted to estimate reinforcement corrosion of concrete structures using infrared thermography method as a method of measuring reinforcement corrosion in concrete. As for the specimen was to measure reinforcement corrosion, D13 reinforcement with size of 200×150×180mm was buried at length of 250mm for covering depth of 20mm and 40mm. Accelerated reinforcement corrosion test was carried out after placement of concrete. As a result of measuring reinforcement corrosion using infrared thermography method, temperature difference of 1~3°C was shown depending on the corrosion stage. There was a correlation in which temperature decreased according to chloride content. Infrared thermography method was confirmed as a useful method for measurement of reinforcement corrosion inside concrete.

본 논문의 목적은 열화상 비파괴 검사기법을 적용시 손상된 콘크리트 구조물의 표면온도를 증폭시키기 위해 사용되는 외부 열원의 효율성을 알아보기 위함이다. 원적외선램프와 할로겐램프의 적용성과 효율성을 서로 비교하였다. 이를 위해 전술한 두 개의 열원을 콘크리트의 내부공극과 FRP쉬트의 비부착 결함 시험체에 적용하였다. 본 연구결과, 원적외선램프가 할로겐램프보다 더 효율적인 것으로 파악되었다. 또한, 손상영역을 효과적으로 검출하기위해서 가우스 필터와 프리윗 마스크 화상처리기법을 혼합한 알고리즘을 제안하였다.

본 논문에서는 비접촉 손상검출기법으로 관심의 대상이 되고 있는 열화상 기법의 기본 원리, 활용 예, 제한 사항 등을 국내외 주요 연구성과를 분석하고 정리하였다. 콘크리트 구조물의 내부 결함 진단, 내부 철근 부식 측정과 콘크리트 구조물 표면과 섬유 보강 시트 사이의 비부착 검출, 포장도로의 표면 결함 검출, 오래된 건물의 표면 누수 측정, 철도 트랙 자갈의 상태 측정 등을 최근 연구결과 중심으로 광범위하게 검토하였고 최근에 보고된 실험결과도 제시하였다. 검토 결과, 열화상 기법은 광범위한 형태의 토목 구조물의 넓은 표면을 빠르게 정성적으로 검사할 수 있는 장점을 가지고 있는 것으로 확인되었다. 반면, 정량적 기법은 주변 온도 등 환경 요인에 민감하게 영향을 받는 것으로 판단되었으며, 다른 정밀계측장비와 혼용시 좋은 성과를 기대할 수 있을 것으로 예측된다.