Recent Engineered nanoparticles were increasingly exposed to environmental system with the wide application and production of nanomaterials, concerns are increasing about their environmental risk to soil and groundwater system. In order to assess the transport behavior of silver nanoparticles (AgNPs), a saturated packed column experiments were examined. Inductively coupled plasma-mass spectrometry and a DLS detector was used for concentration and size measurement of AgNPs. The column experiment results showed that solution chemistry had a considerable temporal deposition of AgNPs on the porous media of solid glass beads. In column experiment, comparable mobility improvement of AgNPs were observed by changing solution chemistry conditions from salts (in both NaCl and CaCl2 solutions) to DI conditions, but in much lower ionic strength (IS) with CaCl2. Additionally, the fitted parameters with two-site kinetic attachment model form the experimental breakthrough curves (BTCs) were associated that the retention rates of the AgNPs aggregates were enhanced with increasing IS under both NaCl and CaCl2 solutions.

The aim of this study is to investigate the sorption/ion exchange of radioactive nuclides such as Cs+ and Sr2+ by synthetic Na-micas. In order to prepare Na-micas, two natural micas (phlogopite and biotite) were used as precursor materials. XRD, SEM, and EDS analyses were used to examine material characterization of synthetic Na-micas. Analyses of materials revealed that Na-micas were successfully obtained from natrual micas by K removal treatment. On the other hand, single solute (Cs or Sr) and bi-solute (Cs/Sr) sorption experiments were carried out to determine sorption capacity of Na-micas for Cs and Sr under different pH and ionic strength conditions. Uptake of Cs and Sr by micas in bi-solute system was lower than in single-solute system. Additionally, Langmuir and Langmuir competitive models were applied to describe sorption isotherm of Na-micas. bi-solute system was well described by Langmuir competitive models. For the results obtained in this study, Na-micas could be promising sorbents to treat multi-radioactive species from water and groundwater.

본 연구에서는 표면 침투 및 코팅형 흡수방지재인 Polydimethylsiloxane(PDMS)을 고인성 섬유복합체(ECC)에 적용하여 적용성, 강도 평가 및 염화물이온 침투 저항성능에 대한 연구를 수행하였다. PDMS 적용 방법에 따른 침투깊이를 분석한 결과 모든 방법에서 KS F4930 의 기준을 만족하는 것을 확인하였다. 적용 방법 중, 침지 방법이 가장 우수한 침투깊이를 보였으나 현장적용성을 고려할 경우 스프레이 방법이 적용 가능한 것으로 확인되었다. ECC 배합에 따른 PDMS 침투깊이 실험 결과 배합강도가 감소할수록 침투깊이는 최대 70% 이상 증가하는 경향을 나타났다. 압축강도 시험 결과에서는 PDMS 침투 깊이가 큰 M4-A, M4-B 시험체의 압축강도는 PDMS를 적용하지 않은 M4 시험체와 비교하여 9.6%, 8.0% 압축강도가 감소하였다. 또한, 침투깊이가 작은 M1-A와 M1-B 시험체의 압축강도는 M1 시험체와 비교하여 4%, 2.2% 감소하여 PDMS 침투깊이가 클수록 강도감소율이 증가하였다. 염소이온침투 저항성능 평가 시험결과, PDMS의 침투깊이가 클수록 염소이온 침투 저항성능이 향상되는 것을 확인하였다.

From the test results, it was found that the compressive strength and the resistance of chloride ion penetration were evaluated the slag content of the concrete for bridge pavement. Compressive strength test results showed that initial strength was decreased as slag replacement ratio increased. The chlorine ion penetration performance increased with increasing strength.

From the test results, it was found that the compressive strength and the resistance of chloride ion penetration were evaluated the slag content of the concrete for bridge pavement. Compressive strength test results showed that initial strength was decreased as slag replacement ratio increased. The chlorine ion penetration performance increased with increasing strength.

메타카올린은 고령토나 카올린으로 알려진 카올린 광물의 풍화물로, 도자기 산업에 주로 사용되는 원료로, 일반적으로 메타카올린의 입자 크기는 시멘트보다는 작지만, 마이크로 실리카퓸보다는 크다. 본 연구에서는 콘크리트용 혼화재로 메타카올린을사용한 콘크리트의 압축강도와 염소이온 투과저항 특성에 관한 영향에 관해 조사하였다. 메타카올린과 실리카퓸의 혼입률이 압축강도와 염소이온 투과저항에 주는 영향을 비교하기 위해 물-결합재비를 30%로 고정하고 각각 0, 5, 10, 15, 20%인 배합수준을 설정하여 비교하였다. 연구결과 메타카올린을 혼입한 콘크리트는 실리카퓸을 혼입한 콘크리트와 유사한 강도특성을 보였지만, 염소이온 투과저항성은 다소 불리한 것으로 나타났다. 따라서, 강도와 염소이온 투과저항 성능을 동시에 만족하기 위한메타카올린의 혼입률은 10% 정도인 것으로 나타났다.

최근 고유동 콘크리트(High Fluidity Concrete 이하 HFC)에 대한 연구는 많은 시공사례와 함께 진행되고 있지만, 콘크리트의 내구성능을 평가하는 항목 중 하나인 염소이온 침투에 대한 연구는 미비하며, 기존의 내구성관련 연구는 고강도 이상(40MPa)연구됨에 따라 보통강도 고유동 콘크리트의 염소이온 침투에 관한 연구는 찾아보기 어려운 실정이다. 따라서 본 연구에서는 석회석 미분말을 혼합한 보통강도 HFC를 제조하여 콘크리트의 공극구조 및 염소이온 침투특성을 분석․고찰 하였다. 실험결과 석회석 미분말을 혼합한 2성분계 및 3성분계 고유동 콘크리트의 경우 콘크리트의 공극 크기는 0.005∼0.05 ㎛ 사이에서 가장 많이 분포 하고 있으며, 석회석 미분말의 혼합률이 증가할수록 평균 공극 직경은 커지는 것으로 나타났다. 또한 석회석 미분말의 혼합률이 증가할수록 염소이온 침투깊이 및 확산계수는 증가하는 경향이 나타나며, 확산계수는 압축강도 및 평균공극직경 사이의 상관관계에서 결정계수 0.90 이상의 양호한 상관성이 있었다.