We evaluated the developed microstructures and mechanical properties of a severely plastically deformed Ni-30Cr alloy. Normal rolling and differential speed rolling were used as deformation processes, and the thicknesses of the specimens were reduced to 68 % of the original thickness after holding at 700 oC for 10 min and annealing at 700 oC for 40 min to obtain a fully recrystallized microstructure. Electron backscattering diffraction was used to analyze the characteristic distribution of the grain boundaries on the deformed and annealed specimens. Differential speed rolling was more effective for refining grains in comparison with normal rolling. The grain size was refined from 33 mm in the initial material to 8.1 mm with normal rolling and 5.5 mm with differential speed rolling. The more refined grain in the differential-speed-rolled material directly resulted in increases in the yield and tensile strengths by 68 % and 9.0%, respectively, compared to normal rolling. We systematically explain the relationship between the grain refinement and mechanical properties through a plastically deformed Ni-30Cr alloy based on the development of a deformation texture. The results of our study show that the DSR process is very effective when used to enhance the mechanical properties of a material through grain refinement.

A two-pass differential speed rolling(DSR) was applied to a deoxidized low-phosphorous copper alloy sheet in order to form a homogeneous microstructure. Copper alloy with a thickness of 3 mm was rolled to 75 % reduction by two-pass rolling at 150˚C without lubrication at a differential speed ratio of 2.0:1. In order to introduce uniform shear strain into the copper alloy sheet, the second rolling was performed after turning the sample by 180˚ on the transverse direction axis. Conventional rolling(CR), in which the rotating speeds of the upper roll and lower roll are identical to each other, was also performed by two-pass rolling under a total rolling reduction of 75 %, for comparison. The shear strain introduced by the conventional rolling showed positive values at positions of the upper roll side and negative values at positions of the lower roll side. However, samples processed by the DSR showed zero or positive values at all positions. 100//ND texture was primarily developed near the surface and center of thickness for the CR, while 110//ND texture was primarily developed for the DSR. The difference in misorientation distribution of grain boundary between the upper roll side surface and center regions was very small in the CR, while it was large in the DSR. The grain size was smallest in the upper roll side region for both the CR and the DSR. The hardness showed homogeneous distribution in the thickness direction in both CR and DSR. The average hardness was larger in CR than in DSR.