In order to prepare high-solid coatings, acrylic resins, HSCs [poly (EA/EMA/2-HEMA/CLA)] that contain 90% solid, were synthesized by copolymerization of ethyl acrylate (EA), ethyl methacrylate (EMA), 2-hydroxyethyl methacrylate (2-HEMA) and caprolactone acrylate (CLA). The high-solid coatings named as CHSCs (HSCs/HDI-trimer) were prepared by the curing reaction between the acrylic resins containing 90% solid contents and the isocyanates (HDI-trimer) curing agent room temperature. The curing behavior and various properties were examined on the film coated with the both high-solid coatings. The glass transition temperatures (Tg) of CHSCs increased proportionally with increasing the predicted Tg value by Fox equation, and had nothing to do with the solid contents. The prepared film showed good properties for 60˚ specular gloss, impact resistance, cross-hatch adhesion and heat resistance, and bad properties for pencil hardness, drying time, and pot-life. Among the film properties, the heat resistance was very excellent and could be explained by the introduction of functional monomers of CLA.

The high-solid coatings were prepared by blending the synthesized acrylic resin in the previous paper, and hexamethylene diisocyanate-trimer and curing it at room temperature. The characterization of the films of the prepared coatings was performed. The 60˚ specular gloss, impact resistance, cross-hatch adhesion, and heat resistance of the films proved to be good, and the pencil hardness, drying time, and pot-life proved to be slightly poor. From a viscoelastic measurement using a rigid-body pendulum, curing was accelerated with the Tg value.

Acrylic resins (HSCs : EA/EMA/2-HEMA/CLA) which contain 80% solid content were synthesized by the copolymerization of monomers (ethyl acrylate, ethyl methacrylate, 2-hydroxyethyl methacrylate) and functional monomer (caprolactone acrylate : CLA) which improves the crosslinking density and physical properties of films. The physical properties of the prepared acrylic resins (HSCs) containing CLA, are as follows: viscosity 1440~2630 cps ; Mn 1590~1660 ; and conversions, 81~86%, respectively. From the correlation of Tg values, viscosities, and Mn of the HSCs, it was found thst viscosity and Mn increased with Tg value.