Cavitation can occur in pipes when liquid is moving at high velocity, especially at pittings where the smooth bore of the pipe is interrupted. The effect is usually to produce pitting on the downstream side of the turbulence. However, stress corrosion cracking behavior under cavitation erosion-corrosion was neatly unknown. In this study, therefore, some were investigated of stress corrosion cracking behavior, others were stress corrosion cracking behavior under cavitation erosion-corrosion of water injection. And datas obtained as the results of experiment were compared between the two. Mainresult obtained are as follows: 1) Stress corrosion cracking growth rate of heat affected zone under cavitation erosion-corrosion becomes most rapid, and stress intensity factor K1becomes most high. 2) Stress corrosion cracking growth mechanism by cavitation erosion-corrosion is judgement on the strength of the film rupture model and the tunnel model. 3) The range of potential as passivation of heat affected zone is less noble than that of base metal, and that value is smaller. 4) Corrosion potential under cavitation erosion-corrosion in loaded stress is less noble than that of stress corrosion, and corrosion current density is higher.

The effect of fluid flow on corrosion and erosion-corrosion of metal is a well-recognized phenomenon in pipelines and machinery equipment, and so on. Not only are fluid hydrodynamics important, but also the corrosiveness of the process or production stream affects the corrosion system. Recent research demonstrates that it is possible to erosion-corrosion(E/C) phenomena in terms of hydrodynamics, electrochemical corrosion kinetics and film growth/removal phenomena. Stress corrosion cracking behavior under cavitation erosion-corrosion of mild steel(SS41) was investigated of base metal and weldment under loaded stress. Main result obtained are as follows : 1) The cavitation erosion sensitivity of base metal affected weight loss is more susceptive than heat affected zone, 2) The corrosion sensitivity affected weight loss of welding heat cycle is less susceptive on stress corrosion under cavitation erosion-corrosion than stress corrosion.

The component materials threatened by cavitation include ship propellers as well as turbine runners, pump impellers, pipe lines and radiators. Today it is known that cavitation damage takes place on many other components including on the coding water side of the cylinder liners of diesel engines. Cavitation erosion - corrosion implies damage to materials due to the shock pressure or shock wave that results when bubbles form and collapse at a metal surface within a liquid. To suppress cavitation erosion as well as cavitation erosion - corrosion to hydraulic equipment, innovations such as the improvement in the geometric design of the equipment or the selection of suitably resistant construction materials are necessary. In this study, we investigated that the cavitation erosion - corrosion damage under vibratory cavitation can be reduced by adding of side now velocity to the cavitation bubble group in order to eliminate bubbles formed in sea water environment.

Cavitation erosion-corrosion implies damage to materials due to the shock pressure or shock wave that results when bubbles form and collapse at a metal surface within a liquid. If the liquids corrosive to the material, a condition typically encountered in industry, the component materials may suffer serious damage by a combination of mechanical and electrochemical attack. To suppress cavitation erosion as well as cavitation erosion-corrosion to hydraulic equipments, innovations such as the improvement in the geometric design of the equipment or the selection of suitably resistant construction materials are necessary. This study was tested by using the piezoelectric vibrator with 20kHz, 24μm for cavitation generation. And also, the vibratory cavitation erosion-corrosion tests on commercial mild steel SS41were carried out. We carefully observed the erosion pattern and surface photography. The geometrical mechanism of pit growth, which is to be likely these processing; shallow typelongrightarrowundercut typelongrightarrowwide shallow type.

각종 환경 조건에서 진동 캐비테이션 침식-부식 시험 장치에 의해 연강(SS41)의 캐비테이션 침식-부식 손상 거동에 관한 연구를 한 결과 다음과 같은 결론을 얻었다. 1) 해수 중에서 캐비테이션 침식-부식 손상 거동은 중앙부와 테두리 부에서 거의 비슷한 정도로 발생하여 성장되지만, 증류수 중에서는 테두리부에서 손상이 먼저 발생한 다음 중앙부에도 손상이 점차 일어난다. 2) 비저항이 낮은 수도수 중의 캐비테이션 침식-부식 손상은 초기에는 비저항이 높은 증류수중에서의 것보다 증가하지만 시간이 경과하면서 CaCO 하(3)의 피막 형성에 의해 둔화된다. 3) 케비테이션 침식-부식 손상 특성은 잠복기, 증가기, 감소기 및 안정기의 4단계로 구분된다.

Recently, with the rapid development in the industries such as an iron mill and chemical plants, there is enlarged by the use of the piping. Sepecially, the piping connected with a fluid, if it is increase the speed of running fluid, ought to generate cavitation phenomenon with unbalanced pressure. So, the cavitation phenomenon cause serious damage of the piping, because it generate erosion and corrosion in the piping. In this study, the steel pipe piping water (SPPW) and SPPW on weldment were tested by using of cavitation-erosion test apparatus with nozzle and were investigated under the marine environment of liquid. (specific resistance : 25 Omega. cm) The main results obtained are as follows : 1) The total weight loss and weight loss rate of affected zone of weldment by corrosion-erosion in the sea water are more increased than that of base metal. 2) The electrode potential by corrosion-erosion in the sea water becomes less noble than that of base metal, and current density is more increased. 3) As time goes by, the total weight loss and weight loss rate by cavitation erosion-corrosion in air-liquid 2 phase flow become more increased then those in only liquid solution. but these values turn to be decreased.