Bi2Sr2CaCu2Ox(Bi-2212) and Bi2Sr2Ca2Cu3Oy(Bi-2223) high-Tc superconductors(HTS) have been manufactured by plasma spraying, partial melt process(PMP) and annealing treatment(AT). A Bi-2212/2223 HTS coating layer was synthesized through the peritectic reaction between a 0212 oxide coating layer and 2001 oxide coating layer by the PMP-AT process. The 2212 HTS layer consists of whiskers grown in the diffusion direction. The Bi-2223 phase and secondary phase in the Bi-2212 layer were observed. The secondary phase was distributed uniformly over the whole layer. As annealing time goes on, the Bi-2212 phase decreases with mis-orientation and irregular shape, but the Bi-2223 phase increases because a new Bi-2223 phase is formed inside the pre-existing Bi-2212 crystals, and because of the nucleation of a Bi-2223 phase at the edge of Bi-2212 crystals by diffusion of Ca and Cu-O bilayers. In this study the spray coated layer showed superconducting transitions with an onset Tc of about both 115 K, and 50 K. There were two steps. Step 1 at 115 K is due to the diamagnetism of the Bi-2223 phase and step 2 at 50 K is due to the diamagnetism of the Bi-2212 phase.

Formation and characteristics of spraying powder for BSCCO High-Tc superconductor prepared by plasma spray coating were investigated. The addition of 3% of binder gives the best flowability of the powder. Ball milling for 30h and 35h gives the best flowability of powder in the case of 2001 and 0212, respectively. The withdraw ratio increases upon binder addition from 12 to 27% in the case of 2001 and from 18 to 31% in the case of 0212 for sieving powder of in size. The built-up efficiency for thickness of spray coating is increased more than 30% by binder addition. The microstructure of the spray coated layers was investigated by XRD and EDS analysis.

Magnetic characteristics observed in BiSrCaCuO superconductor were studied. In the measurement of differential conductance, it was cleared that the mechanism of magnetic memory effect couldn't be explained by using conventional flux flow model. By changing the density of external magnetic flux, changes in inductance of a coil in which a superconducting bar inserted were also measured. The results showed that the filament model was valid to explain the mechanism of the occurrence of a voltage in superconducting sample. It was concluded that the electromagnetic characteristics arose from the interaction between the trapped magnetic flux and weak link of the filament formed in the superconducting bulk.