The addition of fiber sto concrete matrix has been a norm to enhance the mechanical strength of concrete. However, the use ot synthetic fibers (artificial fibers) is rampant compared to natural fibers due to a low mechanical strength of some natural fibers. The study added cellulose fiber made from jute at 0.2%, 0.25, and 0.3% of cement weight to concrete matrix to determine their influence on the early strength development. It was observed that compressive strength and flexural strength increases as the proportion of fiber added to the concrete increased. Further observation showed that the compressive strength had its optimum point at 0.3% fiber addition. However, the optimum point of the flexural strength lied at 0.25% fiber addition. It was concluded that cellulose fiber is capable of enhancing the mechanical strengths of concrete matrix.

PURPOSES : This study describes the experimental findings on the mechanical properties of calcium aluminate cement (CAC)-based repair mortars with or without natural cellulose fiber (NCF). Additionally, the effect of adding NCF to the reduction of fugitive dust in the CAC powder was examined. METHODS : To produce mortar, four different levels of NCF (0.0.5, 1.0, and 2.0% by binder weight) were adopted, and the water-binder ratio was fixed at 0.485. The flow, strength characteristics, absorption, and surface electrical resistivity of the mortars were measured at predetermined periods. Additionally, SEM observations were performed to examine the microstructural changes and hydrates formed on the 28 day-mortar samples. RESULTS : The addition of NCF led to a decrease in fugitive dust. Regarding the mechanical properties of the mortars, that with 0.5% NCF exhibited a better performance in terms of strength development and surface electric resistivity compared to those of other mortars. However, the addition of NCF was less effective in the enhancement of the absorption of mortars. Further, we discovered that the microstructures of the mortars with additional NCF were comparatively dense compared to those without NCF. CONCLUSIONS : The appropriate addition of NCF can enhance the performance of CAC-based repair materials. However, further studies on the durability of CAC with the addition of NCF are needed to determine the optimal mixture.

본 연구에서는 인체 친화적이고 환경 친화적인 패션제품 소재기획을 위한 기초 자료를 제시하고자 수행되었다. 이를 위해서 4종의 섬유소 소재를 대상으로 염색조건을 달리하여 천연 쪽 염색을 실시하여 색채특성과 색채감성을 평가하였으며, 이러한 특성이 선호도에 미치는 영향을 분석하였다. 쪽 염색된 직물은 모두 중, 저명도와 저채도의 남색(PB)을 구현하였다. 이들 직물의 색채특성은 섬유종류와 염색조건에 따라 유의한 차이를 보였다. 쪽 염색된 직물에 대한 색채감성은 스포티 감성, 클래식 감성, 내추럴 감성 등 3가지 요인으로 분류되었다. 이러한 색채감성은 섬유종류와 염색조건에 따라 부분적으로 유의한 차이를 나타내었다. 또한 쪽 염색 직물의 색채특성과 색채감성 요인 간에는 부분적으로 유의한 상관관계를 보였다. 쪽 염색 직물의 색채 선호도에 영향을 주는 요인으로는 색채감성 요인 중에서 클래식 감성과 스포티 감성, 색채특성에서는 L*값인 것으로 나타났다.

The purpose of this research is to revive the colors of combination dyeing and mixed dyeing with natural dyestuffs. The fabrics used were cotton and rayon. The natural dyestuffs used in this research were indigo, Phellodendron amurense, and Caesalpinia sappan. The effects of combination dyeing were as follows. First, all samples showed deeper colors. Second, according to the results of the surface K/S measurement, while the surface K/S of cotton was over 15, that of rayon was over 17. Third, the results of the light fastness measurement showed the superiority (by over grade 4) of all the samples, except in the case of rayon fiber sample no. 6 (which had been pre-dyed with indigo five times before being dyed with P. amurense once and then being dyed with C. sappan once). In the color fastness to washing measurement, all fibers showed superiority (by over grade 3~4). In addition, the color fastness to dry cleaning of all fibers was satisfactory or excellent (by over grade 3). Fourth, according to the results of the tensile strength measurement, it tended to decrease in the case of cotton and increase in the case of rayon. Fifth, the results of the density measurement showed that the density of cotton decreased by about 15~20% in the case of warp and 10% in the case of weft for all samples. The density of rayon decreased 20% in the case of warp for all samples and increased 30% in the case of weft for all samples.

막분리 공정의 응용범위와 시장규모가 증가함에 따라 효과적인 물질분리를 위해 다양한 분리공정이 이용되고 있다. 이중 정수처리공정에서 수질의 안전성, 자동화 등의 장점 때문에 분리막에 대한 관심이 증가되고 있으며, 정수처리에 사용되는 대부분의 분리막은 강한 내구성, 장수명성 등이 요구되어, 이를 위하여 막오염 저항성이 크게 요구된다. 일반적으로 셀룰로오스 계열은 친수성이 강하며 막오염 저항성이 우수하고 정밀여과막이나 한외여과막 소재로 사용된다. 본 연구에서는 고분자량을 갖는 친수성 소재인 아세틸화된 메틸 셀룰로오스를 사용하여 한외중공사막을 다양한 조건에서 제조하고 제조된 막의 구조적 특성 및 투과분리 특성에 대하여 살펴보았다.

Regenerated cellulose fibers were prepared from three pulps containing different degree of polymerization(DP) and α-cellulose contents by dry-jet wet spinning technique with cellulose dope in N-methylmorpholin N-oxide (NMMO). The effect of antioxidant, n-propyl gallate (PG) on the properties of different regenerated celluloses was studied using X-ray diffraction, copper number calculation, and viscometry. The degradaqtion of regenerated cellulose from pulp containing higher DP and lower α-cellulose content was occurred more seriously. The tensile strength and initial modulus of regenerated cellulose fiber obtained from NMMO dope with PG were higher than those of fiber obtained from NMMO dope without PG. All fibers showed the round shape cross section and typical cellulose II crystalline structure.

바이오가스의 고질화 공정에서는 필수적으로 메탄의 손실이 발생하게 된다. 특히 기체분리막을 이용한 바이오가 고질화는 타 공정에 비해 경제적이라는 장점이 있지만 메탄 손실율이 높은 편이다. 메탄 손실율이 줄이기 위해서는 고선택도의 분리막 모듈이 요구된다. 분리막을 이용한 바이오가스 고질화 공정에서 메탄손실율이 높은 이유는 CO2에 의한 가소화(Plasticization)으로 CH4의 투과도가 증가하기 때문이다. Cellulose계열의 고분자는 CO2 가소화에 대한 영향이 적기 때문에 CA(Cellulose Acetate)를 사용하여 고선택도의 분리막 개발이 가능하다. 따라서, 투과도가 높은 막을 개발하기 위해 도프용액의 농도와 에어갭(Evaporation time)을 변화시키면서, CA의 두께와 기공을 조절하여, 고선택도의 CA 분리막을 제막하였다. 비용매 유도상 분리법(NIPS, nonsolvent induced phase separation)을 이용하여 제막하였다. 실험에 사용된 Eastman사의 CA를 더 이상 정제하지 않고 그대로 사용하였으며, 도프용액은 다성계로 중합체(polymer), 용매(solvent), 비용제(nonsolvent)를 혼합하여 분리막을 방사하였다. CA의 함량이 증가할수록 active layer 층이 두꺼워지므로 분리막의 선택도가 증가하는 경향을 보였다. 하지만, CA함량이 증가할수록 support layer의 다공층이 줄어들게 되고 active layer층이 두꺼워지므로 투과도도 함께 줄어들게 된다. CA 21wt%에서의 메탄의 투과도와 선택도는 1.3 GPU 및 33.0이였으며, CA 25wt%에서의 메탄 투과도와 선택도는 0.1 GPU 및 43.6으로 고선택도 분리막을 제막하였다.