After melting glass at a high temperature of about 1,100 degrees in the Cold Crucible Induction Melter (CCIM) of the vitrification facility, radioactive waste is fed into the CCIM to vitrify radioactive waste. Accordingly, since the metal sector of the CCIM contacts the high-temperature molten glass, cooling water is supplied to continuously cool the metal sector. The cooling system is divided into primary and secondary cooling water systems. The primary cooling water flows inside the metal sector of the CCIM to maintain the metal sector within normal temperature, thereby forming a glass layer between the metal sector and the high-temperature melting glass. The secondary cooling system is a system that cools the primary cooling water that cools the metal sector, and removes heat generated from the primary cooling system. In addition, it is designed to stably supply cooling water to the secondary cooling water system through an emergency cooling water system so that cooling water can be stably supplied to the secondary cooling water system in the event of secondary cooling water loss. Therefore, it is designed to maintain the facility stably in the event of loss of cooling water for the CCIM of the vitrification facility.

원자력발전소에서 발생하는 이온교환수지와 가연성잡고체 혼합폐기물을 유리화하기 위하여 유도 가열식 저온용융로를 이용한 실증시험을 수행하였다. 금속 티타늄 고리(Ti-ring)를 이용한 유리의 초기점화에 필요한 에너지는 약 290 kWh로 평가되었다. 혼합폐기물의 투입 중 고주파발생기의 출력은 160∼190 kW로 임피던스는 0.55∼0.65 범위 내에서 안정적으로 유지되었다. 이온교환수지 단독투입 시 보다 가연성잡고체와 혼합 할 경우 CO 발생농도는 1/40 정도로 낮아졌는데, 이는 1.8배 정도 높은 연소에너지를 갖는 가연성잡고체가 혼합폐기물의 완전연소를 유도한 것으로 평가되었다. 혼합폐기물의 공급량에 적당한 최적 산소 버블링에 의해 유리 용탕 내부로의 미연폐기물의 함침은 발생하지 않았으며 유리 용탕은 지속적으로 공정 건전성을 유지하였다. 유리 용탕의 부피가 증가하는 팽창(swelling) 현상 때와 정상 일 때 발생가스를 측정, 비교한 결과 swelling 현상 때는 NO와 같이 환원성 가스의 농도 보다 산화성 기체인 의 농도가 높은 것으로 나타났다. 실증시험에 사용된 이온교환 수지와 가연성잡고체의 각각 투입량은 368kg과 751kg 이었으며, 74 정도의 감용비를 달성하였다.