This study reports an experimental and analytical exploration of concrete columns laterally confined with Fe-based shape-memory alloy (Fe-SMA) spirals. For performing experiments, Fe-SMA rebars with a 4% prestrain and diameter of 10 mm were fabricated and concrete columns with internal Fe-SMA spiral reinforcement were constructed with a diameter of 200 mm and height of 600 mm. An acrylic bar with an attached strain gauge was embedded in the center of the specimen to measure local strains. Experimental variables encompassed the Fe-SMA spiral reinforcement, spacing, and activation temperature. Uniaxial compression tests were conducted after applying active confinement to the concrete columns through electrical-resistance heating. Notably, as the Fe-SMA spiral spacing decreased, the local failure zone length and compressive fracture energy of the prepared specimens increased. Additionally, a model incorporating compressive fracture energy was proposed to predict the stress–strain behavior of the. This model, accounting for active and passive confinement effects, demonstrated accurate predictions for the experimental results of this study as well as for previously reported results.

Due to a lack of the hoop action of lateral reinforcements the effective confining force in rectangular sections reduces compared to circular ones. Therefore, the stress-strain model obtained from the experimental data with circular sections overestimates the lateral confinement effect in rectangular sections, which evaluates seismic safety margin of overall structural system excessively. In this study experiments with laterally-confined square sections have been performed and the characteristic values composing stress-strain model have been analyzed. With introduction of section coefficients, in addition, the new unified stress-strain model applicable to square sections as well as circular ones has been proposed.

In order to avoid collapse of bridges in earthquakes bridge piers are generally designed to attain sufficient ductility. This full-ductility design method has merits for securing the seismic safety readily against strong earthquakes but, it has weakness of high cost design because of excessive safety margin. Recently, in many countries with high seismic technologies, the seismic design concept tends to shift from the collapse prevention design to the performance-based one which requires different performance (damage) levels according to the structural importance. In order to establish this performance-based design method the displacement ductility of confined concrete members should be evaluated quantitatively. And the stress-strain model of confined concrete is indispensible in evaluating displacement ductility. In this study, 6 test groups with different lateral reinforcement ratios were prepared. 10 same specimens with circular section for each group were tested to obtain more reliable test results. The characteristic values necessary for composing the stress-strain model were obtained from experiments. Based on these characteristic values the new stress-strain model modifying the Hoshikuma's one has been proposed.

본 연구는 실험계획법(예: 반응표면계획법) 및 하모니 검색 알고리즘을 통하여 다양한 아스팔트 콘크리트 포장 구조체에 있어 피로균열의 공용성 인자인 인장변형률을 예측하는 모델을 개발하는 방법에 대한 연구이다. 인장변형률을 산정하기 위하여 한국건설기술연구소에서 개발한 유한요소 축대칭해석 프로그램인 KICTPAVE를 이용하여 아스팔트 층과 린콘크리트 층의 접속면에서 발생되는 변형률을 구하여 데이터베이스(D/B)화 하였다. 아스팔트 포장에서 입력변수인 층별 탄성계수 및 두께를 다양한 조건에서 KICTPAVE 프로그램을 수행하여 훈련용 D/B(Training Set)인 변형률의 값들을 구축한 후 반응표면계획법에 근거하여 회귀방정식을 정의하였으며 방정식에 필요한 계수값을 결정하기 위하여 하모니 검색 알고리즘을 이용하였다. 최종적으로 결정된 회귀방정식의 계수값들의 정확성을 검증하기 위해서 훈련용 D/B가 아닌 다른 조건의 입력변수를 이용하여 검증용 D/B(Testing Set)를 구축하고 이를 이용하여 개발된 모델을 검증하였다.

본 논문에서는 압축파괴에너지를 이용하여 고강도 구속콘크리트에 대한 응력-변형률 모델을 제안하였다. 참고문헌[5]에서 저자가 실시한 압축실험에는 변형률 게이지를 부착한 아크릴 막대를 실험체의 중앙부에 매립하여 압축부재의 국부 변형률 측정을 시도하였다. 이 아크릴 막대를 이용한 국부 변형률 측정은 매우 효과적인 것으로 나타났다. 압축파괴영역길이는 아크릴 막대로부터 측정된 국부 변형률 분포에 기초하여 정의되었다. 구체적으로, 구속콘크리트의 국소파괴영역길이는 압축강도 발현시의 변형률 εcc의 2배 이상 변형률이 증가하는 영역으로 정의하였다. 또한, 동일한 횡구속압을 받는 압축부재에 흡수된 에너지양은 부재의 형상이나 크기에 관계없이 일정하다는 가정에서 압축파괴에너지를 도입한 구속콘크리트의 응력-변형률 관계를 제안하였다. 본 연구에서 제안된 모델은 본 연구의 실험결과뿐만 아니라 타 연구자들의 실험결과를 대체적으로 잘 예측하는 것으로 나타났다.

초고강도 콘크리트를 이용한 부재의 내화 성능을 검토하기 위해서는 실제부재 단위의 시험에 의한 평가가 요구되고 있다. 그러나 실제부재 실험을 하기 위해서는 재하 능력이 큰 시험 장비가 필요하기 때문에, 재료 모델을 이용한 해석적 연구를 통해 내화 성능을 평가하고 있다. 본 연구에서는 80, 130 및 180 MPa의 초고강도 콘크리트를 대상으로 고온 가열시의 변형 특성을 실험적으로 평가하고 초고강도 콘크리 트에 대한 기존 변형 모델의 적용을 검토했다. 그 후, 최소 제곱법에 의해 실험 값과 기존의 변형 모델을 적용한 계산 값의 누적 오차가 가장 작 은 상수 값을 도출하고 초고강도 콘크리트에 적용 할 수 있는 변형 모델을 제시했다.