In order to provide the mechanism of nozzle clogging, recovered nozzles for high strength steel grade were examined carefully after continuous casting. The thickness of clogged material in SEN is increased in the following order: from the bottom to the top of the nozzle, upper part of slag line, and the pouring hole. Nozzle clogging material begins to form due the adhesion of metal to nozzle wall, the decarburization, and reduction of oxide in the refractory by Al and Ti in the melt. The reduction of oxide in the refractory by Al and Ti improves the wettability of the melt on the refractory and forms a thin Al-Ti-O layer. Metal containing micro alumina inclusions is solidified on the Al-Ti-O layer, and the solid layer grows due to the heat evolution through the nozzle wall. Thermodynamic calculation has been made for the related reactions. The effect of superheat to the nozzle clogging is discussed on ultra low carbon steel and low carbon steel.

본 연구에서는 반응고 Al합금을 얻기 위해서 3상 2극의 전자교반장치를 이용하였으며, 주입온도와 주입전압을 변화시켜 Al합금의 초정입자크기, aspect ratio, 표준편차, 경도 및 공정 Si 입자의 크기 및 형상 변화를 조사하였다. 같은 주입온도에서는 주입전압이 증가함에 따라 aspect ratio, 표준편차 및 초정입자의 크기는 감소되었다. 전자교반식 수평연속주조방법에 의한 Al 합금의 최적제조 조건은 주입전압 220V, 주입온도 680˚C이었으며, 이 조건에서 초정입자의 크기는 54μm이었고, aspect ratio는 1.56이었으며 그 표준편차는 0.4이었다. 그리고 공정 Si의 크기는 0.5μm이었으며 제조된 Al합금의 경도는 72.1 Hv를 나타내었다. 본 연구를 위해 제작된 3상 2극 전자교반장치에 의해서 매우 낮은 aspect ratio 및 표준편자를 갖는 반응고 A356 Al합금을 제조할 수 있었다.